Biological and mechanical characterization of commercial and experimental periodontal surgical dressings

Abstract

The objective of this study was to evaluate the biocompatibility and mechanical properties of two commercially available and one experimental periodontal dressing materials. The cytotoxicity of Periobond ® , Barricaid ® and one experimental periodontal dressing based on Exothane ® 8 monomer was tested on 3T3/NIH mouse fibroblast. Genotoxicity was assessed by micronuclei formation, and cell alterations were analyzed using light microscopy. Both biological assays were performed using the eluate obtained from specimens after 24, 72, or 168 hours of incubation. Mechanical characterization was assessed through the ultimate tensile strength and the water sorption and solubility tests. The significance level of α = 0.05 was used for all statistical analyses. All the materials promoted a cell viability lower than 60% in all evaluated times. In general, the cell viability was significantly reduced after 72 and 168h of specimens' incubation. Considering the factor material, there were not statistical differences in the cell viability (p = 0.156). The genotoxicity was not statistically significant among the groups in the different periods of time (p > 0.05). Differences in the ultimate tensile strength values were not statistically significant different among the groups (p = 0.125). Periobond ® showed the higher water sorption values (p < 0.001). Regarding solubility, there were no statistical differences between the groups (p = 0.098). All the periodontal dressing materials evaluated in this study exerted a cytotoxic effect against mouse fibroblasts, and their toxicity became more evident over time. Among the materials evaluated, the experimental light-cure type has shown overall similar properties to the commercial references.

Drug Release and Cytotoxicity of Hyaluronic Acid and Zinc Oxide Gels, An In-Vitro Study

“…It was noticed that there was a complete cell death in both HPdLF cells and hGFs. Hence, we diluted the sample in a 1:100 ratio as described previously, resulting in total cell mortality [ 28 ]. These results strongly correlate with the present study as many other studies on the toxicity of zinc oxide on human cell lines, questioning the use of zinc oxide in commercially available periodontal dressings used on periodontal surgical wounds [ 29 , 30 ].…”

Çi̇nko-Oksi̇t Non-Öjenol Patlardaki Boyutsal Deği̇şi̇mi̇n Üç Boyutlu İncelenmesi̇

“…2,3 Bu amaçla çok sayıda materyal üretilmiş ve halen deneysel olarak geliştirilmektedir. 3,4 İdeal bir periodontal patın manipülasyonu kolay olmalı, düzgün ve oral mukozayı irrite etmeyen bir yüzeyi olmalı, ağız içerisindeki hareketlerle deformasyona karşı dirençli olurken elastisitesini korumalı, dental dokulara iyi bir adezyon ile tutunmalı, plak ve tükürük akümülasyonunu engellemek için boyutsal olarak stabil olması gerektiği bildirilmiştir. 5,6 Ticari olarak sunulan ideal bir periodontal pat ürünün bulunmadığı bildirilmiştir.…”

“…7 Periodontal patların hücresel düzeyde sitotoksik olduğunu ve erken dönemde bakteri kolonizasyonunu engellerken geç dönemde artmasına sebep olduğunu gösteren çalışmalar bulunmaktadır. 4,8 Periodontal patlar çeşitli kimyasal reaksiyonlarla veya ışıkla aktive edilerek sertleşmeleri sağlanmaktadır. 4 Bu reaksiyonlar sonrasında değişen yapısal özellikleri, adezyonları, iyon salınımları ve boyutsal değişimleri ile ilgili çalışmalar yapılmıştır.…”

“…4,8 Periodontal patlar çeşitli kimyasal reaksiyonlarla veya ışıkla aktive edilerek sertleşmeleri sağlanmaktadır. 4 Bu reaksiyonlar sonrasında değişen yapısal özellikleri, adezyonları, iyon salınımları ve boyutsal değişimleri ile ilgili çalışmalar yapılmıştır. 9,10 Periodontal patların kullanım alanlarından birisi de greft stabilizasyonudur.…”