Characterisation of the Microstructure of Plain Carbon Steel Formed during Isothermal and Continuous Cooling Following Austenitisation

Abstract

The present study has been undertaken to compare the microstructure of the plain carbon steel, containing 0.65 carbon, which was formed during varying isothermal and continuous cooling conditions following austenitisation at the same temperature and soaking time. After austenitisation, one set of samples was subjected to isothermal treatment which was carried out at a temperature varying in the range of 650–400 °C, and the other one was continuously cooled to ambient temperature using different cooling rates ranging from 500 to 1.4 °Cs–1. The metallographic examination of the samples was fulfilled using light and TEM microscopy. Additionally, Vickers hardness measurements were performed.