Chitosan capped Silver nanoparticles used as Pressure sensors

Silver nanoparticles (AgNPs) were prepared by employing green chemicals such as gallic acid as reductant and starch as a stabilizer. The maximum absorption peak at 443 nm of the synthesized nanoparticles was observed in UV-visible spectrum. The existence of the fcc structure of silver nanocrystal with intense diffraction peak along (111) plane with a crystallite size of 9.32 ± 1.31 nm was evidenced from XRD studies. Quasi-spherical AgNPs of average diameter 48.42 ± 14 nm, hexagonal AgNPs with mean edge length 31.75 ± 7.29 nm and triangular AgNPs of mean edge length 48.55 ± 11.37 nm were confirmed from the TEM images. FTIR analysis verified that the synthesized AgNPs were stabilized by starch. The AgNPs was used as a catalyst in the alkaline hydrolysis of crystal violet dye. A 2.41 × 10-2 min-1 and 4.49 × 10-2 min-1 were degradation rate constants of crystal violet in the absence and presence of silver nanoparticles, respectively. The results clearly highlighted that the green synthesized silver nanoparticles can be used as catalyst in the degradation of toxic dyes in industrial effluents and environment.

show abstract

Chitosan capped Silver nanoparticles used as Pressure sensors

Cited by 3 publications

References 28 publications

Polymers-Metal Nanocomposites

Polymers-Metal Nanocomposites

Synthesis of Ag nanoparticles by a chitosan-poly(3-hydroxybutyrate) polymer conjugate and their superb catalytic activity

Catalytic Activity of Green Synthesized Silver Nanoparticles on Alkaline Hydrolysis of Crystal Violet Dye

Contact Info

Product

Resources

About