Coarsening of Al3Sc precipitates in Al-Mg-Sc alloys

131

Thermal stability, determining the material ability of retaining its properties at required temperatures over extended service time, is becoming the next frontier for aluminum alloys. Its improvement would substantially expand their range of structural applications, especially in automotive and aerospace industries. This report explains the fundamentals of thermal stability; definitions, the properties involved; and the deterioration indicators during thermal/thermomechanical exposures, including an impact of accidental fire, and testing techniques. For individual classes of alloys, efforts aimed at identifying factors stabilizing their microstructure at service temperatures are described. Particular attention is paid to attempts of increasing the current upper service limit of high-temperature grades. In addition to alloying aluminum with a variety of elements to create the thermally stable microstructure, in particular, transition and rare-earth metals, parallel efforts are explored through applying novel routes of alloy processing, such as rapid solidification, powder metallurgy and additive manufacturing, engineering alloys in a liquid state prior to casting, and post-casting treatments. The goal is to overcome the present barriers and to develop novel aluminum alloys with superior properties that are stable across the temperature and time space, required by modern designs.

Section: Exploring Scandium To Improve Thermal Stability Of Almentioning

confidence: 96%

Thermal Stability of Aluminum Alloys

Czerwiński

2020

131

“…In a severer condition, the Al 3 Sc phase inevitably coarsens and loses its reinforcing effect at ~400 • C [28][29][30]. Therefore, some micro-alloyed elements (Zr/Ti/Yb/Gd/Y) are co-incorporated with Sc to improve the high-temperature stability of the precipitated phase.…”

Section: Introductionmentioning

confidence: 99%

Optimizing the Heat Treatment Method to Improve the Aging Response of Al-Fe-Ni-Sc-Zr Alloys

Wang,

Bian,

Zhu

et al. 2024

This work has studied the co-addition of Sc and Zr elements into the Al-1.75wt%Fe-1.25wt%Ni eutectic alloy. The changes in the microstructure, electrical conductivity, and Vickers hardness of the Al-1.75wt%Fe-1.25wt%Ni-0.2wt%Sc-0.2wt%Zr alloy during heat treatment were studied. The results showed that two-step aging can effectively improve the aging response of the alloy over the single-step aging method. This was ascribed to the minimization of the diffusion difference between Sc and Zr elements. Furthermore, the homogenization treatment can also improve the aging response of the alloy by alleviating the uneven distribution of Sc and Zr. Nevertheless, the micro-alloyed elements exceeded the solid solubility limit in the Al-1.75wt%Fe-1.25wt%Ni-0.2wt%Sc-0.2wt%Zr alloy, and their strengthening effect has ever achieved the best prospect. Finally, both Sc and Zr contents were reduced simultaneously, and the aging response of the Al-1.75wt%Fe-1.25wt%Ni-0.15wt%Sc-0.1wt%Zr alloy was improved by optimized heat treatment. The underlying mechanisms for this alloy design and the corresponding microstructure–mechanical property relationship were analytically discussed.

“…In recent years, a large number of studies have proved that microalloying can effectively improve the mechanical properties and corrosion resistance of aluminum alloys [ 7 , 8 , 9 ]. In this study, a small amount of Zn, Er, and Zr elements were added to the traditional Al−Mg alloy.…”

Section: Introductionmentioning

confidence: 99%

Effect of Zr and Er Addition on the Microstructural Evolution of a Novel Al−Mg−Zn−Er−Zr Alloy during Hot Compression

Wei

Zuo

et al. 2023

The hot compression experiment of homogenized Al−5.2Mg−0.6Mn−0.29Zn−0.16Er–0.12Zr alloy was carried out by the Gleeble-3500 thermal simulation testing system. The deformation behavior in temperatures of 350~500 ℃ and deformation rates of 0.01~10 s−1 was studied. The relationship between stress and strain rate and deformation temperature was analyzed. The constitutive equation of alloy high-temperature deformation was constructed by the Zener–Hollomon method, and the hot working diagram with the true strain of 0.2 and 0.5 was constructed according to the dynamic material model. The research results show that flow stress has a positive correlation with strain rate and a negative correlation with temperature. The steady flow stress during deformation can be described by a hyperbolic sinusoidal constitutive equation. Adding Er and Zr into Al−Mg alloy can not only refine grains and strengthen precipitation but also form a core–shell Al3(Er, Zr) phase. In the deformation process, Al3(Er, Zr) precipitates can pin dislocations and inhibit dynamic recrystallization (DRX). Dynamic recovery (DRV) is dominant during hot deformation. The mechanism of dynamic recovery is dislocation motion. At high temperatures, Al3(Er, Zr) can also inhibit grain coarsening. The average hot deformation activation energy of the alloy is 203.7 kJ/mol. This high activation energy can be due to the pinning effect of Er and Zr precipitates. The processing map of the alloy was analyzed and combined with the observation of microstructure, the hot deformation instability zone of the alloy was determined, and the suitable process parameters for hot deformation were obtained, which were 450~480 °C, and the strain rate is 0.01~0.09 s−1.