Ultrasonic vibration was employed in blending the nanosilica into epoxy resin to manufacture hemp/kevlar/nanosilica-based epoxy composites, with an ultrasonic occurrence of 20 kHz and a 900 W capacity of power. An ultrasonic probe was utilized to ensure the consistent dispersion of the nanoparticles in the epoxy. The mechanical characteristics of hemp/kevlar fiber reinforced with epoxy/nanosilica in a mat form have been studied. Hand layup procedures were used to create these composites, including varying weight % of nanosilica and variable fiber stacking sequencing. The different weight % are 3, 6, and 9, and the stacking sequences are B, C, and D. The effectiveness of ultrasonic irradiation on mechanical characteristics was investigated and related. The inclusion of 6 wt.% of SiO2 to the B type resulted in a 25% rise in tension and a 37% in bending. The addition of 6 wt.% silica to the C-type hybridization nanocomposite results in a 34% rise in tension and a 38% rise in bending. Extreme tension behavior is attained at 6 wt.% SiO2 with epoxy with the B type piling order, and extreme bending behavior is obtained at 6 wt.% SiO2 with the C type piling order. A B-type model composite with a 6-wt.% SiO2 addition performed better in hygroscopic than A, C, and D type model composites. An SEM is utilized to observe the microstructure of shattered materials.

Section: Flexuralsupporting

confidence: 70%

Influence of Epoxy/Nanosilica on Mechanical Performance of Hemp/Kevlar Fiber Reinforced Hybrid Composite with an Ultrasonic Frequency

Velmurugan

Rao

et al. 2022

“…It indicates the bonding strength using fibre pull-out [46]. The pull-out rage is higher for initial parameter specimens than optimal specimens [47].…”

Section: Resultsmentioning

confidence: 99%

Effect of Nano TiO₂ Filler Addition on Mechanical Properties of Bamboo/Polyester Hybrid Composites and Parameters Optimized Using Grey Taguchi Method

Kumar

Sethupathy³

et al. 2022

Exploration has shifted from traditional materials and alloys to composite materials in recent years to develop lightweight, high-effective materials for specific purposes. Natural fibres are less costly, biodegradable, and nonflammable than glass fibres. This study explores how titanium oxide affects woven polyester reinforced composite’s mechanical and physical characteristics. Nanocomposites were created by hand utilizing the following terms: (i) TiO2 nanoparticle filler weight ratio, (ii) fibre content, and (iii) fibre diameter, all at three unique levels. Using the L9 (33) orthogonal design, nine composite samples are generated and tested according to the ASTM standard. According to the research, hybrid composites containing 4% titanium oxide powder and 15 mm length of bamboo fibre with 0.24 mm of bamboo fibre diameter have high mechanical strength. Adding fibre to pristine polyester increased its mechanical properties. As the fibre and filler percentages grew, more effort was required to break the fragments between the matrix and its resin. The verification test, which uses the optimal processing value and grey relational analysis, outperforms the real test results by a wide margin. Tensile strength increased by 14.76%, flexural strength increased by 14.07%, and hardness increased by 25.55%.

“…The current study studied the water retention properties of nanocomposites using two types of solutions (ordinary tap water and nanofluid). The composite system has greater retention properties than regular water in a nanofluid environment [44]. When nanocomposites are submerged in nanofluid, the interface attraction between reinforcements, fillers, and matrix increases dramatically.…”

Section: Flexural Strengthmentioning

confidence: 99%

Water Retention Behaviour and Fracture Toughness of Coir/Pineapple Leaf Fibre with Addition of Al₂O₃ Hybrid Composites under Ambient Conditions

Kumar

Sethupathy³

et al. 2022

Due to their high mechanical and physical properties, natural fibre-based composite materials have been important in many fields of application for four to five years. The chief intention of the current study is to determine the mechanical and water retention features of composite materials under ambient conditions. Coir and pineapple leaf fibre were used as a reinforcement, aluminium oxide as additives, and polyester as a matrix. The hybrid resources were laminated by the manual hand lay-up method. The mechanical characteristics like tensile, flexural, and fracture toughness properties were tested as per the ASTM standard. Nanoparticle weight ratio and its size variation significantly impact mechanical qualities. The hybrid composite’s water retention behaviour was tested for two types of water levels: ordinary tab water and nanofluid. The moisture uptake of the composites rose as the fibre volume increased, and after 640 hours, all of the composites had reached equilibrium. According to the results, the following combinations have the maximum mechanical strength: 15% wt.% coir, 15% wt.% pineapple, 10% wt.% nanofiller, and 60% wt.% polyester resin. The combinations mentioned above withstand the most load during the tests. Compared to 20% filler, 10% Al2O3 filler produces good interfacial adhesion in the current study. The fractured specimens were analyzed using scanning electron microscopic (SEM) pictures to recognize better the failure process of composites during mechanical testing.