Comparison of the quenching capacities of hot salt and oil baths

Help me understand this report

Search citation statements

Order By: Relevance

Paper Sections

Select...
2
1
1

Citation Types

1
3
0

Year Published

2008
2008
2023
2023

Publication Types

Select...
7
1

Relationship

0
8

Authors

Journals

citations
Cited by 13 publications
(4 citation statements)
references
References 1 publication
1
3
0
Order By: Relevance
“…The hardness value of the annealed weldment sample was observed to be slightly lower than the HAZ region, this could be as a result of the grain growth of ferrite and pearlite grains in the weldment (plate 2a, b). However, the quenched weldment and HAZ samples exhibited the highest hardness values of about 108HRB and 56.2 HRB respectively; this could be as a result of the high cooling rates which led to the formation of hard and brittle marten site phase (plate 3a, b).This is in agreement with the report of Rassizadehghani et al, [9]. Figure 5 shows the impact strength (energy absorbed per unit area under the notch) for the PWHT structures produced by subjecting the welded samples to normalizing, annealing, hardening (quenching by water) treatments.…”
Section: Resultssupporting
confidence: 90%
“…The hardness value of the annealed weldment sample was observed to be slightly lower than the HAZ region, this could be as a result of the grain growth of ferrite and pearlite grains in the weldment (plate 2a, b). However, the quenched weldment and HAZ samples exhibited the highest hardness values of about 108HRB and 56.2 HRB respectively; this could be as a result of the high cooling rates which led to the formation of hard and brittle marten site phase (plate 3a, b).This is in agreement with the report of Rassizadehghani et al, [9]. Figure 5 shows the impact strength (energy absorbed per unit area under the notch) for the PWHT structures produced by subjecting the welded samples to normalizing, annealing, hardening (quenching by water) treatments.…”
Section: Resultssupporting
confidence: 90%
“…Thus, the mechanical strength of medium carbon steels can be improved by quenching in appropriate medium. However, the major influencing factors in the choice of the quenching medium are the kind of heat treatment, composition of the steel, the sizes and shapes of the parts [5].…”
Section: Introductionmentioning
confidence: 99%
“…As the operating temperature of molten salt bath is in the range of 150-700 C [41], the prediction of total entropy generation of balls injected in molten salt for three temperature difference, namely, 70 K, 150 K and 250 K is shown in Figure 14.…”
Section: Effect Of Initial Temperature Difference and Injection Velocmentioning
confidence: 99%