Complex Characteristics of Sintered Nd-Fe-B Magnets in Terms of Hydrogen Based Recycling

Abstract

Sintered Nd-Fe-B magnets, dismantled by the P.P.H.U. Polblume company from scrap hard disc drives and medical device, were thermally demagnetized and analyzed in terms of their chemical composition, structure and magnetic properties. Magnets from hard disc drives drives had a magnetic structure of two opposite poles in a plane of a magnet and were covered with a nickel coating (around 50 µm in thick), which however was often discontinuous and deeply scratched. The majority of the magnets were partially destroyed (broken or corroded). The magnet from hard disc drives were basically made of iron (65±1 wt%) and neodymium (30±2 wt%) however, they also included alloying elements such as Co (1-2.5 wt%), Dy (0-1 wt%) or Pr (0-5 wt%). The magnets from medical device consisted only of iron (65±1 wt%) and neodymium (34±1 wt%). Magnets of both kinds were textured thus their XRD patterns were amended. Diffraction patterns, typical for the Nd2Fe14B (ϕ) phase, were achieved after mechanical crushing of the bulk magnets. A regular X-ray diffraction pattern was achieved after mechanical crushing of the magnets. The microstructure of both types of the magnets, observed by scanning electron microscopy, consisted of grey grains of a Nd2Fe14B (ϕ) phase and a Nd-rich grain boundary phase. The magnets from hard disc drives exhibited excellent magnetic properties and anisotropy: maximum energy product above 300 kJ/m 3 , remanence around 1.4 T and coercivity around 1000 kA/m, slightly varying between each magnet. Magnetic properties of medical magnet were only a little worse: maximum energy product above 200 kJ/m 3 , remanence around 1.1 T and coercivity around 900 kA/m. Hydrogen disproportionation phase diagrams (temperature vs. pressure) were constructed for both kinds of the magnets, revealing possible conditions for the hydrogenation, disproportionation, desorption and recombination reaction.