Copper oxide and niobium pentoxide supported on silica-alumina: Synthesis, characterization, and application on diesel soot oxidation

Braga, Vítor; Garcia, Fillipe A.C.; Dias, José A.; Dias, Sílvia C.L.

doi:10.1016/j.jcat.2006.12.022

Cited by 40 publications

(29 citation statements)

References 35 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Also, it is employed for the design and fabrication of nanosensors, nanolasers, switches and transistors [21,22] and is good selective solar absorber since it possesses high solar absorbency and low thermal emittance [23]. A CuO is widely used as a pigment in ceramics, as dispersed nanoparticles in nanofluids to increase thermal conductivity [24], as catalyst in the abatement of NO x [25], superconductor [26], gas sensors [27], magnetic storage media [28], lithium-ion electrode materials [29], solar cells [30], field transistors and biosensors, etc. [31,32].…”

Section: Introductionmentioning

confidence: 99%

Electrochemical bulk synthesis and characterisation of hexagonal-shaped CuO nanoparticles

Chandrappa

Venkatesha

2012

Journal of Experimental Nanoscience

View full text Add to dashboard Cite

A simple and efficient two-step hybrid electrochemical-thermal route was developed for the bulk synthesis of CuO nanoparticles using aqueous sodium nitrate electrolyte and Cu electrodes in an undivided cell under galvanostatic mode at room temperature. The influence of electrolyte concentration on the synthesis of CuO nanoparticles was studied at 1.0 A/dm 2 current density. Electrochemically generated precursor was calcined for an hour at different levels of temperature in the range 200-900 C. The calcined samples were characterised by XRD, TG-DTA, XPS, SEM/ EDAX, TEM, FT-IR and UV-Vis spectral methods. The crystallite sizes were estimated and the thermal behaviour of as-prepared compound was examined. Rietveld refinement of X-ray data shows results matching the monoclinic structure with the space group of C2/c (no. 15). The TEM result revealed that the particle sizes were in the order of 30-50 nm diameter and 120-200 nm length. The blue shift was noticed in UV-Vis absorption spectra. All samples of CuO exhibited randomly oriented hexagonal morphology.

show abstract

Section: Introductionmentioning

confidence: 99%

Electrochemical bulk synthesis and characterisation of hexagonal-shaped CuO nanoparticles

Chandrappa

Venkatesha

2012

Journal of Experimental Nanoscience

View full text Add to dashboard Cite

show abstract

“…New catalytic materials containing copper oxide and niobium pentoxide supported on silica-alumina (CuO/ Nb 2 O 5 /SiO 2 -Al 2 O 3 ) have recently been characterized under distinct preparation conditions, oxide loadings (including sub-monolayer, monolayer and above-monolayer coverage) and calcination temperatures [14]. A strong influence was observed for the CuO over Nb 2 O 5 crystallites, according to preparation method [10,14].…”

Section: Introductionmentioning

confidence: 99%

“…A strong influence was observed for the CuO over Nb 2 O 5 crystallites, according to preparation method [10,14]. The most promising materials contained a 1:1 oxide ratio (CuO:Nb 2 O 5 ), were prepared by simultaneous impregnation, and calcined at 300°C.…”

Section: Introductionmentioning

confidence: 99%

“…The most promising materials contained a 1:1 oxide ratio (CuO:Nb 2 O 5 ), were prepared by simultaneous impregnation, and calcined at 300°C. It was determined the surface species composition as isolated CuO x and/or Nb 2 O x as well as polymerized Nb 2 O x at lower coverage (2-5 mass%); whereas at higher coverage (10-25 mass%) crystalline CuO and amorphous Nb 2 O 5 were observed [14].…”

Section: Introductionmentioning

confidence: 99%

See 1 more Smart Citation

Acidic Characterization of Copper Oxide and Niobium Pentoxide Supported on Silica–Alumina

et al. 2007

View full text Add to dashboard Cite

Copper oxide and niobium pentoxide were supported on silica-alumina with 2, 5, 10, 15 and 25 mass% loadings and 1:1 mass ratio of CuO:Nb 2 O 5 . XRD and BET measurements confirmed that monolayer coverage is reached with loadings between 5-10 mass% (~308 m 2 g -1 ). The DRIFTS spectra of pyridine adsorbed catalysts showed bands associated with Brönsted, Lewis and a combination of both acidic sites. Thermal analysis and liquid phase microcalorimetry provided the parameters for the best catalyst (10 mass%), which has the highest number of acidic sites (0.38 mmol g -1 ) and enthalpies of interaction with pyridine for Brönsted and Lewis sites (DH 1 = -107.5 and DH 2 = -64.4 kJ mol -1 , respectively).

show abstract

“…En la figura 2 (a), correspondiente al KNN puro, se presenta una banda alrededor de ~550 cm -1 que pertenece al modo vibracional del NaNbO 3 y/o KNbO 3 [16], la banda alrededor de ~768 cm -1 está asociada al modo vibracional del enlace Nb-O del octaedro NbO 6 [17] y la banda alrededor de ~662 cm -1 corresponde a la vibración del octaedro NbO 6 , indicando la existencia de la fase perovskita [18,19]. Cuando el KNN se dopa con 0.5 % de BLFO (figura 2 (b)), las bandas anteriormente mencionadas experimentan un corrimiento y aparecen nuevas bandas.…”

Section: Parte Experimentalunclassified

Efecto del BiFeO3 en las propiedades del sistema ferroeléctrico libre de plomo K0.5Na0.5NbO3

Pinza¹,

Jurado²,

Raigoza³

2014

Bol. Soc. Esp. Ceram. Vidr.

View full text Add to dashboard Cite

INTRODUCCIÓNUno de los enfoques prometedores para crear nuevos materiales es la combinación de diferentes propiedades físicas en un material para aumentar su funcionalidad. El acoplamiento entre los parámetros de orden magnético y ferroeléctrico puede conducir a efectos magnetoeléctricos, en los que la magnetización puede ser modificada por la aplicación de un campo eléctrico y viceversa. A la fecha han sido identificados relativamente pocos materiales multiferroicos, y en los que se conocen, el mecanismo que subyace a su ferroelectricidad es a menudo poco convencional [1]. El niobato de potasio y sodio, K 0.5 Na 0.5 NbO 3 (KNN), se ha considerado un buen candidato para la fabricación de cerámicas ferroeléctricas libres de plomo debido a su buena respuesta piezoeléctrica y la relativamente alta temperatura de Curie ~420 ºC [2]. Sin embargo, es muy difícil sinterizar cerámicas piezoeléctricas basadas en KNN debido a la volatilidad del Na y del K y a su alta reactividad con la humedad. Por otro lado el BiFeO 3 es un compuesto multiferroico muy utilizado recientemente debido a que sus temperaturas de transición eléctrica y magnética, están encima de la temperatura ambiente (T C ∼ 820-850 ºC, T N = 370 ºC) siendo un óptimo candidato para el desarrollo de aplicaciones. Uno de los grandes problemas con este compuesto es la presencia de impurezas que aumentan la conductividad eléctrica, enmascarando el fenómeno de la ferroelectricidad [3]. Por otro lado, el BiFeO 3 (BFO) se ha usado como dopante del KNN para formar contorno de fase morfotrópico (CFM) romboédrico-ortorrómbico [4]. Sin embargo, la solubilidad del BFO en KNN es pequeña, lo que se atribuye a la gran diferencia estructural entre ambos materiales (BFO romboédrico y KNN ortorrómbico); para aumentar la solubilidad del BFO en el KNN puede ser útil la sustitución del sitio A por lantano ya que puede desviar su estructura de romboédrica a tetragonal/ortorrómbica a temperatura ambiente, por ejemplo, la estructura del sistema (Bi 0.8 La 0.2 )FeO 3 (BLFO) es tetragonal [4]. La obtención de cerámicas densas basadas en KNN depende fuertemente de las características del polvo de partida, por esto deben utilizarse métodos de síntesis que garanticen el control estequiométrico, disminución de la temperatura de síntesis y sinterización, la reproducibilidad, etc. El método de reacción por combustión se destaca como un importante y moderno procedimiento para la síntesis instantánea de óxidos cerámicos multicomponentes, En la búsqueda de un material multiferroico, se prepararon polvos y piezas cerámicas del sistema ferroeléctrico libre de plomo (1-x)K 0.5 Na 0.5 NbO 3 -x(Bi 0.8 La 0.2 )FeO 3 (KNN-BLFO) (x=0.005, 0.010, 0.015, 0.020, 0.025), mediante el método de reacción por combustión. Para todas las estequiometrias estudiadas se obtuvo la fase perovskita característica del KNN. Con las diferentes caracterizaciones se determinó que el BLFO se incorpora en la estructura cristalina del KNN modificándola sin que se presente una transición de fase. Se comprobó además que la adic...

show abstract

Copper oxide and niobium pentoxide supported on silica-alumina: Synthesis, characterization, and application on diesel soot oxidation

Cited by 40 publications

References 35 publications

Electrochemical bulk synthesis and characterisation of hexagonal-shaped CuO nanoparticles

Electrochemical bulk synthesis and characterisation of hexagonal-shaped CuO nanoparticles

Acidic Characterization of Copper Oxide and Niobium Pentoxide Supported on Silica–Alumina

Efecto del BiFeO<sub>3</sub> en las propiedades del sistema ferroeléctrico libre de plomo K<sub>0.5</sub>Na<sub>0.5</sub>NbO<sub>3</sub>

Contact Info

Product

Resources

About