Corrosion Performance of Epoxy/Sulfur–Selenium Coating on Q235 Steel

Abstract

Sulfur powder (99.99%) and selenium powder (99.99%) were mixed and heated to approximately 300 °C to obtain an S-Se alloy. It has good flowability at 130 °C and can be applied to Q235 steel to obtain a S-Se coating. Epoxy was used as a filler, and the S-Se alloy was applied as a coating. This combination was utilized to create the composite coatings of epoxy/sulfur–selenium (E/S-Se). To investigate the corrosion resistance of this coating on Q235 steel substrate, we conducted measurements and obtained electrochemical impedance spectra (EIS) and linear polarization curves (LPC). These measurements were performed in a three-electrode cell within an electrochemical workstation using a 3.5 wt.% NaCl aqueous solution. By comparing bare Q235 steel, S-Se, and E/S-Se, the study found that the E/S-Se coating had a higher self-corrosion potential (−0.484 V vs. SCE) and the lowest self-corrosion current density (2.361 × 10−11 A/cm2). The purpose was to simulate the corrosive environment experienced by condensate return pipe walls in petroleum refining equipment. Additionally, experiments were carried out using 0.01 mol/L HCl solution as the corrosion medium at different temperatures (40 °C, 60 °C, 80 °C). The results indicated that the E/S-Se coating exhibited a lower corrosion rate compared to the Q235 steel substrate. Under immersion conditions at 40 °C and 60 °C, no corrosive substances were detected on the surface of the coating. The test results demonstrated that the E/S-Se coating exhibited superior corrosion resistance compared to the Q235 substrate, providing up to 99% protection for the substrate.

Synthesis of an Epoxy Toughening Curing Agent through Modification of Terephthalic Acid Sludge Waste

“…Epoxy resins (EP) are highly versatile thermosetting materials that find applications in various fields, including paints [12][13][14], binders [15,16], structural components, and electronic materials [17]. This versatility stems from their excellent physical and electrical characteristics, superior bonding ability, and outstanding chemical stability [18,19].…”