Desenvolvimento de sistema de apoio com depósito cerâmico para soldagem e processamento por atrito com pino não consumível

Santos, Tiago Felipe de Abreu; Ea, Torres; Hermengildo, Tahiana F. C.; Ramírez, Antonio J.

doi:10.1590/0104-9224/si1902.02

Cited by 3 publications

(3 citation statements)

References 31 publications

(33 reference statements)

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Los resultados de los ensayos de doblado así como otros detalles relacionados con la realización de las juntas soldadas pueden ser consultados en Santos et al (2014). Al considerar como parámetro de evaluación el desplazamiento de la herramienta (D E ), resulta claro que se obtuvieron juntas con aporte tér-mico (AT) diferente, como se presenta en la Fig.…”

Section: Juntas Soldadas Y Evolución De La Temperaturaunclassified

Inhibition of the formation of intermetallic compounds in aluminum-steel welded joints by friction stir welding

López¹,

Ramírez²

2015

REVMETAL

Self Cite

View full text Add to dashboard Cite

RESUMEN:La unión de juntas aluminio-acero, sin la formación de fases deletéreas del tipo Fe x Al y , ha sido, por décadas, un desafío para los procesos de soldadura. La soldadura por fricción-agitación ha sido empleada para intentar reducir el aporte térmico y evitar la formación de compuestos intermetálicos. Usando esta técnica fueron soldadas juntas disimilares de aluminio 6063-T5 y acero AISI-SAE 1020. La soldadura fue acompañada de medidas de temperatura durante su ejecución. La interfase de las juntas soldadas fue caracterizada utilizando microscopía óptica, electrónica de barrido y electrónica de transmisión. Adicionalmente fueron realizadas medidas puntuales X-EDS y DRX. Los resultados experimentales revelan que la temperatura máxima en la junta es inferior a 360 °C. La caracterización microestructural en la interfase aluminio-acero demostró la ausencia de compuestos intermetálicos, condición atribuida al uso de parámetros de soldadura con bajo aporte térmico. ABSTRACT: Inhibition of the formation of intermetallic compounds in aluminum-steel welded joints by friction stir welding.Formation of deleterious phases during welding of aluminum and steel is a challenge of the welding processes, for decades. Friction Stir Welding (FSW) has been used in an attempt to reduce formation of intermetallic compounds trough reducing the heat input. In this research, dissimilar joint of 6063-T5 aluminum alloy and AISI-SAE 1020 steel were welded using this technique. The temperature of welded joints was measured during the process. The interface of the welded joints was characterized using optical microscopy, scanning and transmission electron microscopy. Additionally, composition measurements were carried out by X-EDS and DRX. The experimental results revealed that the maximum temperature on the joint studied is less than 360 °C. The microstructural characterization in the aluminum-steel interface showed the absence of intermetallic compounds, which is a condition attributed to the use of welding with low thermal input parameters.

show abstract

Section: Juntas Soldadas Y Evolución De La Temperaturaunclassified

Inhibition of the formation of intermetallic compounds in aluminum-steel welded joints by friction stir welding

López¹,

Ramírez²

2015

REVMETAL

Self Cite

View full text Add to dashboard Cite

show abstract

“…Figure 1 shows a schematic drawing of FSW with all the zones mentioned above. DSS 28 and SDSS 29 do not show HAZs on both sides (AS and RS) of the welded joint. The formation of different regions and the presence of several metallographic phases cause variations in the mechanical and microstructural properties of the metal, which makes it necessary to determine whether such features are improved or worsened.…”

Section: Introductionmentioning

confidence: 78%

“…This backing plate has been described previously 29 . The welding process was developed in two stages: preliminary and final joining.…”

Section: Methodsmentioning

confidence: 99%

Friction stir welding of duplex and superduplex stainless steels and some aspects of microstructural characterization and mechanical performance

et al. 2016

View full text Add to dashboard Cite

Friction stir welding was used to produce butt joints on 6 mm thick plates of UNS S32101 lean duplex stainless steel, S32205 duplex stainless steel, and S32750 and S32760 superduplex stainless steels. Fully consolidated joints were achieved, with full penetration, using heat input of 1.37-1.50 kJ/mm. Specimens submitted to tensile testing performed perpendicular to the welding direction showed failure on the base metal, reflecting better mechanical performance of the welded joints. Furthermore, tensile testing along the joints revealed higher yield and tensile strengths in all cases, as well as increased elongation. Microstructural evaluation showed that there was pronounced grain refinement in the welded joints of all the materials studied, achieving grain sizes as small as 1 µm. The differences in the ferrite and austenite grain sizes in the stir zone, such as the degree of grain refinement, could be explained by the combination of dynamic recrystallization of austenite during the welding process and the recrystallization and growth of the ferrite grains, promoted firstly by the severe deformation and secondly by the high temperature inherent to the FSW process. Superduplex stainless steel FSW joints were more able to maintain a balanced microstructure, compared to conventional and lean duplex stainless steels, due to greater homogeneity of recrystallization in the welded joint.

show abstract

Detailed Microstructural Characterization and Restoration Mechanisms of Duplex and Superduplex Stainless Steel Friction-Stir-Welded Joints

Santos

Lippold

et al. 2016

J. of Materi Eng and Perform

View full text Add to dashboard Cite

Desenvolvimento de sistema de apoio com depósito cerâmico para soldagem e processamento por atrito com pino não consumível

Cited by 3 publications

References 31 publications

Inhibition of the formation of intermetallic compounds in aluminum-steel welded joints by friction stir welding

Inhibition of the formation of intermetallic compounds in aluminum-steel welded joints by friction stir welding

Friction stir welding of duplex and superduplex stainless steels and some aspects of microstructural characterization and mechanical performance

Detailed Microstructural Characterization and Restoration Mechanisms of Duplex and Superduplex Stainless Steel Friction-Stir-Welded Joints

Contact Info

Product

Resources

About