Detection of Phase Transformation during Plastic Deformation of Metastable Austenitic Steel AISI 304L by Means of X-ray Diffraction Pattern Analysis

Abstract

This paper evaluates the suitability of the X-ray diffraction (XRD) technique to characterize the phase transformation during the metal forming of the metastable austenitic steel AISI 304L. Due to plastic deformation, phase transformation from γ-austenite into α’-martensite occurs. The XRD peaks at specific 2θ diffraction angles give information about the phase amount. Analyses of the results with different characterization techniques such as microscopic analysis, including electron backscatter diffraction (EBSD), macro- and microhardness tests and magneto-inductive measurements of α’-martensite, were carried out. A qualitative and quantitative correlation to compute the amount of α’-martensite from the XRD measurements was deduced. XRD was validated as a suitable technique to characterize the phase transformation of metastable austenites. Additional data could provide necessary information to develop a more reliable model to perform a quantitative analysis of the phases from XRD measurements.