Determination of Thermal Diffusivity and Influence of Defect Structure in Alloys Based on the Fe-Al System

Abstract

Alloys of the Fe-Al system are interesting due to occurrence of long-range order and many thermal vacancies at high temperature, which lead to not only significant hardening, but also cause changes of physical properties. High temperature diffusion is conditioned by structural defects in solids, such as vacancies, foreign atoms and dislocations influencing thermal characteristics of a solid solution, among others the thermal diffusivity coefficient. Measurement of thermal diffusivity was performed at room temperature using the laser flash method. For characterization of the defect structure, positron annihilation lifetime spectroscopy was used. The data were presented for alloys with 28 and 38 at.% aluminium without chromium and containing 5 at. % Cr addition. The results showed that thermal diffusivity decreased with aluminium content and deviation from stoichiometry. In the studies, different structural defects in the alloys were observed.

Thermal and structural analysis of high-tin bronze of chemical composition corresponding to the composition of the singing bowl

“…As it is commented by the author of [16], it indicates the presence of a second-order transition between β and γ. Additional confirmation for this assumption can be the presence of thermal effect occuring also during cooling (570°C) that shows good compatibility with order-disorder transition observed in alloys from Ni-Al-Cr or Fe-Al systems [17][18][19][20].…”