Dry sliding wear and mechanical investigations on flyash particulates - Lapinus fibre - polyamide 66 polymer composites: Ranking analysis using hybrid Analytic Hierarchy Process-R method

Abstract

This research work examines the physical, mechanical, thermal, thermo-mechanical, and dry sliding wear performance of hybrid waste flyash particulates (F-class; 0-20 wt% @ step of 5%) – Lapinus fibres (fixed 10 wt%) reinforced Polyamide 66 polymer composites fabricated using the twin screw extruder and injection moulding machine. This follows worn surface morphology to understand the prevailing wear mechanisms responsible for surface damage during sliding. Optimization of control parameters and identification of their order of significance in the dry sliding wear process is performed using Taguchi’s design of experiments and analysis of variance (ANOVA). Further, ranking optimization of the hybrid composite specimens based on their performance metrics is analysed using the hybrid AHP-R method. It has been observed that the hybrid composite specimens having 10 wt% flyash particulates optimize the overall performance metrics; therefore, it may be recommended to fabricate parts or components for industrial usage. It tends to have an experimental density of 1.18 g/cc, voids content of 7.11%, water absorption of 3.87%, tensile strength of 105.95 MPa, flexural strength of 144.86 MPa, Rockwell hardness of 58.12 HRM, fracture toughness of 4.11 MPa√m, Impact strength of 1.86 J, thermal conductivity of 1.08 W/mK, and specific wear rate of 1.12 × 10−3 mm3/Nm. This observation was attuned to the ranking analysis using the hybrid AHP-R method.

The hemp-reinforced polypropylene composite: Effect of the alkaline and coupling agents treatment

“…Polymer composites are intensively studied as replacements in common applications in many industrial fields due to their wide range of properties, such as aerospace, automotive, construction, marine, transportation, electronics, agriculture, furniture, packaging, and sports. [1][2][3][4][5][6][7][8] Polymer composite materials are the combination of two or more materials with different properties in a product that has superior characteristics over the individual component. 9,10 One component is called a matrix and embeds the other component, which is called the reinforcement.…”