Effect of Admixtures on Durability and Physical-Mechanical Properties of Alkali-Activated Materials

Abstract

The results of ground granulated blast furnace slag (GGBS) tests in alkali-activated systems show that, with its use, it is possible to produce promising materials with the required properties. Unfortunately, GGBS is becoming a scarce commodity on the market, so the effort is to partially replace its volume in these materials with other secondary materials, while maintaining the original properties. This paper focuses on a comparison of two basic types of mixtures. The first mixture was prepared only from ground granulated blast furnace slag (GGBS) and the second type of mixture was prepared with admixtures, where the admixtures formed a total of 30% (15% of the replacement was fly ash after denitrification—FA, and 15% of the replacement was cement by-pass dust—CBPD). These mixtures were prepared with varying amounts of activator and tested. The experiment monitored the development of strength over time and the influence of different types of aggressive environments on the strength characteristics. Thermal analysis and FTIR were used in the experiment to determine the degradation products. The paper provides an interesting comparison of the resistance results of different composites in aggressive environments and at the same time an evaluation of the behavior of individual mixtures in different types of aggressive environment. After 28 days of maturation, the highest strengths were obtained with mixtures with the lowest doses of activator. The difference in these compressive strengths was around 25% in favor of the mixtures with only GGBS; in the case of flexural strength, this difference was around 23%. The largest decreases in strength were achieved in the XA3 environment. This environment contains the highest concentration of sulfate ions according to the EN 206-1 standard. The decreases in compressive strength were 40–45%, compared to the same old reference series. The surface degraded due to sulfate ions. Calcium sulphate dihydrate was identified by FTIR, thermal analysis and SEM as a degradation product.

The Effects of Nano-Based Bio-Carbonates in Superhydrophobic Concrete—A Review

“…For the X-ray diffraction (XRD), Mercury intrusion porosimetry (MIP), and nanoindentation experiments, a concrete mixture specimen with a water-cement ratio (w/c) of 0.5 was made and molded into 20 mm × 20 mm × 80 mm [81]. A cement specimen was then produced and molded in molds approximately 102 mm × 102 mm × 102 mm for macroscopic studies such as moisture content, moisture intake rate, and resilience tests.…”