Effect of natural flours on crystallization behaviors of poly(3‐hydroxybutyrate‐co‐3‐hydroxyhexanoate)

Abstract

This paper investigates the effects of natural flours on the crystallization behavior of poly(3‐hydroxybutyrate‐co‐3‐hydroxyhexanoate) (PHBH). Two types of PHBH (3‐hydroxyhexanoate [3HH] contents of 5.6 and 11.1 mol %) were used as polymer matrix. One of two natural flours (cellulose or wood) at 1 wt % was added to this PHBH matrix. Crystallization behaviors under nonisothermal conditions were characterized using differential scanning calorimetry (DSC), while those under isothermal conditions were characterized using DSC and polarized optical microscopy. The results suggested that both cellulose and wood flour addition enhanced crystallization of the PHBH containing 5.6 mol % of 3HH (i.e., increased crystallization peak temperature and degree of crystallinity under the nonisothermal conditions, as well as decreased crystallization half time under the isothermal conditions). Of the two flours, wood flour was found to have greater effects, due to its higher crystal nucleating ability. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016, 133, 43600.

Characterization of biocompatible scaffolds manufactured by fused filament fabrication of poly(3-hydroxybutyrate- co -3-hydroxyhexanoate)

“…Specifically, we observe glass transition at T g = 2°C, cold exothermal crystallization at T cc = 58°C, and two melting peaks: the first, T m1 , at 112°C, and the second and final, T m2 , at 130°C. This bimodal melting pattern, typical of polyesters, was already observed for this copolymer in [ 27 , 36 ]. This behaviour is due to the presence of crystals melting and reorganizing into new crystals with higher structural perfection, which are more stable and melt at higher temperature, namely T m2 .…”

New biocomposite obtained using poly(3‐hydroxybutyrate‐co‐3‐hydroxyhexanoate) (PHBH) and microfibrillated cellulose

“…The thermal properties of the samples were investigated by a Differential Scanning Calorimeter (DSC 2010, TA Instruments), under nitrogen atmosphere, in order to evaluate the glass transition temperature (T g ) and the melting temperature (T m ) of the obtained composites. The crystallinity degree (X c ) of PHBH matrix was calculated by the following equation: where (= 146 J/g) is the enthalpy of 100% crystalline PHB, w f is the mass fraction of filler, and ΔH m is the measured enthalpy of melting.…”

“…), cellulose and wood flours (Deepika et al . ) and fibrillated nanocellulose (Valentini et al . ) have been conducted.…”

“…A particular interest has been reserved to cellulose derivates, due to their biocompatibility, biodegradability, and interesting mechanical properties . Nano and micro cellulose derive from the most abundant and natural polymer, cellulose, which can be produced not only from plants, but also from microorganism, such as bacteria, and in this case, it is called bacterial cellulose (BC).…”

Accelerated biodegradation testing of slowly degradable polyesters in soil

“…The soils were air-dried for 3 days at room temperature and sieved over 2 mm to remove plant remains, stones and other inert materials. a Data found in literature for Nodax type of polymers [34]).…”