Effect of voids on failure mechanisms in RTM laminates

Vārna, Jānis; Joffe, Roberts; Berglund, Lars A.; Lundström, T. Staffan

doi:10.1016/0266-3538(95)00024-0

Cited by 137 publications

(87 citation statements)

References 3 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…The results show that while the fibre dominated mechanical properties are not significantly influenced by voids [1,2,3,4], the matrix dominated properties are strongly dependent on their presence. Reduction in interlaminar shear [1,5,6], compressive [7,8], transverse [1,2], bending [1,3,9], fatigue [4,10,11,12] and fracture toughness [13,14,15] properties have been reported.…”

Section: Introductionmentioning

confidence: 92%

“…Varna et al [2] analysed the effect of voids on failure mechanisms in glass-fibre/vinylester fabric laminates produced by RTM and showed that increasing the void content decreased the transverse static strength. Results indicate an increase in the ultimate transverse strain to as high as 2% at high void content, whereas at low void content the laminates failed at 0.3%.…”

Section: Introductionmentioning

confidence: 99%

“…Wisnom [5], proposed an analytical expression to predict the interlaminar shear strength starting from the Greszczuk's approach to evaluate the net section in the presence of void [17]. The ultimate tensile strain has been studied by Varna [2], who proposed a simple model to explain the large strain to failure of high void content laminates.…”

Section: Introductionmentioning

confidence: 99%

See 2 more Smart Citations

Mode I Strain Energy Release Rate in composite laminates in the presence of voids

Ricotta

Quaresimin

Talreja

2008

Composites Science and Technology

View full text Add to dashboard Cite

ACCEPTED MANUSCRIPT MODE I STRAIN ENERGY RELEASE RATE IN COMPOSITE LAMINATES IN THE PRESENCE OF VOIDS Mauroof the voids is investigated by a parametric study that showed that the enhancement of SERR increases with the size of the voids and the proximity to the crack tip and that elongated (elliptical) voids are more critical than the circular voids. Finally, the influence of more complex void distributions on the fracture toughness is evaluated by FE analysis.

show abstract

Section: Introductionmentioning

confidence: 92%

Section: Introductionmentioning

confidence: 99%

Section: Introductionmentioning

confidence: 99%

See 1 more Smart Citation

Mode I Strain Energy Release Rate in composite laminates in the presence of voids

Ricotta

Quaresimin

Talreja

2008

Composites Science and Technology

View full text Add to dashboard Cite

show abstract

“…However, RTM results in more voids in the laminate due to entrapment of air bubbles during filling [1,2]. Voids are known to be detrimental to the mechanical performance of the material [3][4][5][6][7][8][9][10]. A deeper understanding of the formation of voids, and their effect on damage and mechanical performance is desirable in the context of improving the performance of RTM and other non-autoclave manufactured components.…”

Section: Introductionmentioning

confidence: 99%

“…Previous work has investigated the influence of voids on mechanical properties [3][4][5][6][7][8][9][10], most having focused on prepreg materials. As the microstructure and constituents in composites manufactured with resin infusion processes are usually different from those in autoclave-cured prepregs, the effects of defects on mechanical properties must still be established in RTM composites to pave the way for determining design allowables for the void contents.…”

Section: Introductionmentioning

confidence: 99%

High-resolution computed tomography in resin infused woven carbon fibre composites with voids

Sisodia

Garcea

George

et al. 2016

Composites Science and Technology

View full text Add to dashboard Cite

Significance of paperRecent efforts in the composites industry towards less-expensive means to produce high-performance parts have often involved optimisation of liquid composite moulding processes such as resin transfer moulding (RTM). The most significant gap in part quality between RTM manufactured parts and traditional autoclave processes is the usually higher void content in the former, arising from the entrapment of bubbles during infusion, and the lower consolidation pressures used during such processes. Many laboratories around the world are working on understanding bubble entrapment and subsequent bubble mobility, so as to optimise RTM processes to reduce the concentration and size of voids. This paper contributes to that understanding with threedimensional examination using CT imaging of the morphology, size, clustering and location of the individual voids in composite parts made with RTM. Most important / novel contributionsThis paper presents visualisation of the voids in a composite part with significantly more statistical information regarding size distribution, orientation and location than has been previously shown in the literature. It also addresses a reinforcement architecture more typical to RTM, an un-balanced weave, than the unidirectional fabrics usually studied in previous work on void formation. Analysing a complex reinforcement along with the enhanced visualisation abilities of the CT-imaging technique allowed novel observations and conclusions regarding voids: 1) As the orientation angle between a reinforcement layer and the resin flow direction increases from parallel to perpendicular, larger voids and a greater number of voids were observed in that layer. This was linked to the resulting greater propensity for fatigue crack propagation between voids in layers transverse to the loading direction. A simple optimisation strategy is thus to infuse in a direction transverse to the expected primary load direction, thus creating the fewest voids in the transverse-to-load direction. 2) Voids accumulate around both the layer interfaces and yarns and are nearly completely absent from the layer thickness between those interfaces and away from yarns. 3) Void distribution follows the orientation of fibres in adjacent layers, suggesting that out-of-plane flow is a significant mechanism in void formation and mobility. 4) Observations 1-3 above all imply that current void formation and mobility models must be expanded from a microscale approach to the laminate scale, in order to focus on out-of-plane bubble movement and yarn bubble entrapment. M A N U S C R I P T A C C E P T E D ACCEPTED MANUSCRIPT AbstractTomographic imaging using both microfocus radiation and synchrotron radiation was performed to assess the void defects in resin transfer moulded woven carbon fibre composites. The focus of this study is on characterising the void homology (e.g. local void size and spatial distribution) in relation to weave orientation, infusion direction and potential effects on damage formation in tensile loadin...

show abstract

The Molding Technologies of Polymer Matrix Wave‐Transparent Composites

2024

Polymer Matrix Wave‐Transparent Composites

View full text Add to dashboard Cite

Effect of voids on failure mechanisms in RTM laminates

Cited by 137 publications

References 3 publications

Mode I Strain Energy Release Rate in composite laminates in the presence of voids

Mode I Strain Energy Release Rate in composite laminates in the presence of voids

High-resolution computed tomography in resin infused woven carbon fibre composites with voids

The Molding Technologies of Polymer Matrix Wave‐Transparent Composites

Contact Info

Product

Resources

About