Effects of calcium silicate synthesized in situ on Fiber loading and paper properties

Abstract

The in-situ synthesis of calcium silicate in the fiber can not only meet the requirements for high loading of paper, but also make up and improve the reduction of paper performance caused by filling. In this investigation, the effects of pulp type, beating degree, fiber ratio, reaction time, rotational speed, dosage of lime milk and dispersant on calcium silicate loading and paper properties were investigated. The results showed that when the beating degree was 40 °SR, the ratio of softwood and hardwood pulp was 1:1, the reaction time was 60 min, the rotation speed was 600 r·min−1, the dosage of lime milk was 1.33 times of the theoretical amount, and the dosage of cationic polyacrylamide was 0.3 % (absolutely dry pulp), the ash content of hand-made sheet was 41.2 %, and the loading amount of calcium silicate was 26.3 %. Under this condition, the comprehensive performance of paper was the best.