Effects of excess Bi2O3 on grain orientation and electrical properties of CaBi4Ti4O15 ceramics

Cho, Sam Yeon; Choi, Gi Ppeum; Jeon, Do Hyun; Johnson, Trent; Lee, Min Ku; Lee, Gyoung Ja; Bu, Sang Don

doi:10.1016/j.cap.2015.07.019

Cited by 17 publications

(1 citation statement)

References 20 publications

Supporting

Mentioning

Contrasting

Order By: Relevance

“…In all photographs, the platelet-like morphology of aurivillius-type compounds is evident. the samples did not show delamination that usually occurs when this type of compound is prepared by the solid-state method [11]. the fact that all the microstructures are similar in nature showing plate-like bonded structures may be explained by the molten salt process did not lead to apparent changes in shape and size of the particles.…”

Section: Resultsmentioning

confidence: 74%

Archives of Metallurgy and Materials

Afqir

Elaatmani

Zegzouti

et al. 2022

View full text Add to dashboard Cite

Structure and dielectric ProPertieS of V and Y diSorder doPed SrBi 2 nb 2 o 9 ceramicS Y and V codoped Srbi 2 nb 2 o 9 ceramics, which have been characterized by Xrd, ftir and SeM techniques, were prepared through molten salt using naCl-KCl medium. through X-ray diffraction analysis, all prepared samples were matched by undoped Srbi 2 nb 2 o 9 . the lattice parameters do not depend on the amount of dopants. under the optimized experimental conditions, the compounds are composed of small crystallites of varying size and orientation, resulting in many micros train defects. ftir spectra revealed that the dopant promotes a slight decrease in the 612 cm -1 band. a plate-like morphology was revealed by scanning electron microscopy, while nyquist plots indicate non-debye relaxation for all compounds. V and Y were incorporated into Srbi 2 nb 2 o 9 lattice in order to reduce dielectric loss tangent. thus, the codoping increases the of Srb 1.9 Y 0.1 nb 1.95 V 0.05 o 9 (Y0.1V0.05) ceramic whereas, they were significantly decreased in the case of Srbi 1.8 Y 0.2 nb 2 o 9 (Y0.2) ceramic. Y0.1V0.05 sample makes up the highest efficient charge transfer, followed by Y0.2 sample representing the lowest.

show abstract

Section: Resultsmentioning

confidence: 74%