Electrical and optical properties of thermally evaporated LiBO2–LiF composite films

Abstract

Optical and electrical properties of the LiBO,-LiF composite thin films prepared by thermal evaporation have been studied for their use as ion conductors in solid-state electrochrornic (EC) systems. All the LiBOz-LiF films exhibited a high degree of optical transmission (over 90%) and the best lithium ion conductivity attainable was about 8X 10e7 S cm-', a value considerably higher than that for the ionic conductivity of LiBOz. A typical activation energy of 0.545 eV was found for the composite film. The films obtained thus have a good potential for use as ion conductors in EC devices. 0 1995 American Institute of Physics.

Ιονική Συμπεριφορά Υάλων-Ηλεκτρολυτών Δύο Δομικών Φάσεων Για Συσσωρευτές Στερεάς Κατάστασης

“…Οι βορικές ύαλοι αγωγής ιόντων λιθίου του συστήµατος Li 2 O-B 2 O 3 , ειδικότερα, έχουν µελετηθεί στη βιβλιογραφία ως πιθανοί στερεοί ηλεκτρολύτες σε µορφή λεπτών υµενίων για την κατασκευή µικροσυσσωρευτών [9][10][11]. Με στόχο την αύξηση της ειδικής ιονικής αγωγιµότητας στα λεπτά υµένια, έχουν προταθεί διάφορες παραλλαγές στη βασική ποιοτική σύσταση των βορικών υάλων ιόντων λιθίου, είτε µε την προσθήκη επιπλέον προσµίξεων αλάτων του λιθίου, όπως LiF [12] και Li 2 SO 4 [13], είτε µε τη χρήση, πέραν του B 2 O 3 , και δεύτερης ένωσης σχηµατισµού του υαλώδους δικτύου, όπως SiO 2 [14] και P 2 O 5 [15]. Στην πρώτη περίπτωση, η αύξηση της αγωγιµότητας επιτυγχάνεται µε την εισαγωγή επιπρόσθετων ιονικών φορέων στην ύαλο, καθώς και ως συνέπεια των δοµικών µεταβολών που επάγονται από την ενσωµάτωση των ανιόντων του άλατος.…”