Electroslag surfacing of end faces with large-section electrode in current-supplying mould

Abstract

According to the algorithm of a developed comprehensive analytical solution method (CASM), a new cast high-temperature corrosion-resistant nickel alloy ZhS3LS-М has been developed for manufacture of all-cast nozzle appliances. The developed alloy is characterized by the high-temperature strength 975 40 s = 180-200 MPa at the level of the industrial non-corrosion-resistant alloy VZhL12E as well as technological weldability and corrosion resistance at the level of commercial weldable corrosion-resistant alloy ZhS3LS. 24 Ref., 11 Tables, 1 Figure.

Control of the process of base metal penetration at end face electroslag surfacing in current-supplying mould

“…В частности, на характеристики процесса наплавки влияют длина и расположение кабелей. Например, в случае ЭШН в ТПК диаметром 200 мм при токах до 3 кА и длине кабелей порядка 10 м падение напряжения на них может достигать 15…25 В. Кроме того, необходимо учитывать наличие «вентильного эффекта» в шлаковой ванне [5], который вносит нелинейность и искажает форму синусоиды при подключении источников питания переменного тока [6,7]. Этот же эффект необходимо принимать во внимание при выборе полярности подключения к кристаллизатору источников постоянного тока.…”