Environmental barrier coatings (EBCs) are a commercially proven means of protecting SiC-based materials in gas turbine environments. However, there are little specific data in the literature on the impact of coatings like Yb 2 Si 2 O 7 on preventing accelerated SiO 2 growth in the presence of H 2 O. Quantification of reduced rates are necessary for evaluating and comparing EBC effectiveness and incorporation of silica growth rates into future EBC lifetime models. In this study, baseline kinetics of silica formation on bare Si and chemically vapor deposited (CVD) SiC in the 1250-1425℃ range were obtained via 100 h isothermal exposures in dry air and steam environments utilizing a SiC reaction tube to mitigate specimen volatility. An Arrhenius plot of the resulting rates was constructed, representing baseline minimum and maximum rates for Si and SiC oxidation at ambient pressure. Various EBC systems on CVD SiC substrates including air plasma sprayed (APS) EBCs with and without a Si bond coating and with surface roughening to enhance Yb 2 Si 2 O 7 adhesion were subjected to 1-h furnace cycle testing in air with 90vol%H 2 O at 1250-1350℃ for up to 500 cycles. After exposure, silica formation rates were measured and compared to the baseline rates to assess EBC effectiveness, where EBC effectiveness is gauged as the propensity to reduce underlying rates of silica formation. With a Si bond coating, a ~180 µm Yb 2 Si 2 O 7 (YbDS) top coating reduced rates over the entire 1250°-1350℃ range. Without a Si bond coating, ~60 µm (YbDS) coatings deposited directly onto CVD SiC exhibited poor adhesion, and had to be deposited onto substrates with enhanced roughness at 1350℃. While exhibiting good adhesion at 1350℃, overall the single layer YbDS coating exhibited a decreasing effectiveness from 1250° to 1350℃.