Evaluation of Growth, Thermal, and Spectroscopic Properties of Er3+-Doped CLNGG Crystals for Use in 2.7 μm Laser

Abstract

A series of optical-quality Er3+-doped calcium lithium niobium gallium garnet (CLNGG) single crystals with different Er3+ ion concentration (10, 15 and 30 at.%) has been grown by the Czochralski method. A comparative study of their structure, thermal, and spectroscopic properties is performed. Crystal structure was analyzed with X-ray powder diffraction (XRPD) and refined by the Rietveld method, results showing that the Er:CLNGG crystal possesses a cubic structure with space group Ia3¯d, and the lattice constants decrease linearly as the Er3+ concentration increase. The complete set of thermal properties were systematically studied for the first time. It has been found that all the thermal conductivities increase with temperature, indicating a glass-like behavior. Effect of Er3+ concentration on spectroscopic properties of Er:CLNGG crystals was studied. Results show that with the Er3+ concentration increase, the NIR fluorescence around 1600 nm weakens, while the Mid-IR fluorescence intensity around 2700 nm strengthens. Fluorescence lifetime of 4I13/2 decreased faster than that of 4I11/2 with the Er3+ concentration increase, which is beneficial for surmounting the “bottleneck” effect to achieve 2.7 μm laser. All the results show that CLNGG crystal with high Er3+ concentration is a potential candidate for the 2.7 μm laser.

Development of the 2.7 μm to 3 μm Erbium-Doped Laser

“…Meanwhile, research into laser gain substances is still expanding. New gain stances such as Er:GGAG have been discovered [24][25][26]. There are still problems regar low optical to optical efficiency and serious thermal effects in the existing high sin pulse energy Er laser.…”