Experimental investigations of various joinery methods on repaired AISI 304 A plate with Nitinol wire

Kripalani, Kavita; Jain, Piyush

doi:10.1016/j.matpr.2020.07.522

Cited by 3 publications

(1 citation statement)

References 13 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Por sua vez, caso haja na região uma transformação que acarrete na redução do teor (%) de cromo na solução sólida, esta passa a ser susceptível a corrosão. Este fenômeno se faz presente entre 400 e 800°C, é chamado de sensitização, e ocorre pela combinação de elementos que possuem afinidade pelo cromo como o carbono, nitrogênio que formam carbonetos e nitretos, respectivamente (KRIPALANI et al, 2021;KUMAR et al, 2019).…”

Section: Aços Inoxidáveis Austeníticosunclassified

Influência Do Aporte De Calor Na Microestrutura Da Zona Fundida Do Aço Inoxidável Austenítico Aisi 301

et al. 2021

View full text Add to dashboard Cite

Objetivou-se com esta pesquisa avaliar os efeitos da variação da energia de soldagem na microestrutura da zona fundida do aço inoxidável AISI 301 quantificando a ferrita delta e observando os efeitos desta fase na zona fundida. Para a quantificação da ferrita delta, foi utilizado o software Granulômetro Semi-Automático (GSA). Foram confeccionados cinco corpos de prova, utilizando-se distintos parâmetros de soldagem. O processo de soldagem utilizado foi o Tungsten Inert Gas (TIG). Os resultados mostraram que a energia de soldagem tem grande influência na quantidade de ferrita delta presente na zona fundida e que ocorreu a redução de ferrita delta com o aumento da energia de soldagem.

show abstract

Section: Aços Inoxidáveis Austeníticosunclassified

Influência Do Aporte De Calor Na Microestrutura Da Zona Fundida Do Aço Inoxidável Austenítico Aisi 301

et al. 2021

View full text Add to dashboard Cite

show abstract

Present status and future trend of friction stir-based fabrication of NiTinol: a review

Datta

Bhattacharjee²,

Biswas³

2022

Weld World

View full text Add to dashboard Cite

Comparative Study of Metal-Mineral Abrasive Wearresistance of Hardfacing Layersproduced Through Different Methods

Łatka,

Płatek,

Szala

et al. 2024

Tribologia

View full text Add to dashboard Cite

This article presents a comparison of the results of metal-mineral abrasion resistance investigations of hardfacinglayers produced through different welding methods: (i) arc, (ii) plasma, and (iii) laser. Flux-cored wirewith a metallic core (SK600-G) was used as a feedstock material. The work investigated the influence of basichardfacing parameters on the geometry, microstructure, and correctness of making single beads . Then, fulllayers were made with the parameters selected for each method and abrasion resistance tests were carried outin accordance with the ASTM G65 standard. The obtained test results were analyzed for mechanical propertiesand microstructure of the produced padding welds. On the basis of the tests and analysis of the results,it was found that the use of methods with high energy density has a positive effect on the reduction in thecoefficient of the share of the base material in the padding weld, while increasing the hardness. Comparativeanalysis of the resistance to metal-mineral abrasive wear showed that the resistance was approx. 25% higherfor plasma layers and approx. 35% for laser layers, compared to electric arc-deposited layers.

show abstract

Experimental investigations of various joinery methods on repaired AISI 304 A plate with Nitinol wire

Cited by 3 publications

References 13 publications

Influência Do Aporte De Calor Na Microestrutura Da Zona Fundida Do Aço Inoxidável Austenítico Aisi 301

Influência Do Aporte De Calor Na Microestrutura Da Zona Fundida Do Aço Inoxidável Austenítico Aisi 301

Present status and future trend of friction stir-based fabrication of NiTinol: a review

Comparative Study of Metal-Mineral Abrasive Wearresistance of Hardfacing Layersproduced Through Different Methods

Contact Info

Product

Resources

About