Experimental Study of Stepped-Lap Scarf Joint Repair for Spar Cap Damage of Wind Turbine Blade in Service

Abstract

The objective of this paper was to design configuration parameters for a stepped-lap scarf joint repair, which can be used for spar cap damage of a wind turbine blade in service and to realize the post-repair monitoring. Two experimental studies were included. First, tensile test for the unidirectional tape specimens with a large aspect ratio repaired using a multiple stepped-lap scarf joint method was carried out. The results showed that the reinforcement layer could effectively improve the load-carrying capacity of the repaired zone. The stepped-lap joint surface was identified as the weak part of the spar cap repair, which should be monitored. Second, by embedding carbon nanotube buckypaper sensors on the stepped-lap joint surface of the repaired specimens, quasi-static tensile tests and fatigue tests were carried out. According to the resistance response of the sensors, the quasi-static tensile test confirmed the failure processes, namely the stiffness turning point, damage evolution, crack propagation, and fracture. The fatigue test could accurately identify the progressive failure, namely the initial damage, damage accumulation, initial cracking, and crack propagation to structural failure. The above tests provided an important configuration parameter basis for evaluating the spar cap repair scheme and presented a promising method for the health monitoring of a spar cap after repair.