1998
DOI: 10.1016/s0964-1807(98)00093-3
|View full text |Cite
|
Sign up to set email alerts
|

Fabrication of melt-textured Nd123 superconductors with Nd2BaO4 addition

Help me understand this report

Search citation statements

Order By: Relevance

Paper Sections

Select...
1
1
1
1

Citation Types

3
12
0

Year Published

2002
2002
2017
2017

Publication Types

Select...
8

Relationship

0
8

Authors

Journals

citations
Cited by 17 publications
(15 citation statements)
references
References 30 publications
3
12
0
Order By: Relevance
“…We can see that the particle size of trapped Nd422 particles (dark color) ranges from 1 ∼ 9 μm and from 1 ∼ 15 μm for the samples with and without Nd242, respectively, indicating that the sizes of the Nd422 particles were reduced due to the addition of Nd242. A commensurate phenomenon of reduction in size of LRE211 was also reported for LRE123 bulks with the addition of Barich phases, e.g., LRE210 or LRE242 [18,[20][21][22][23]. Specifically, the particle size of Nd422 ranged from 1 ∼ 12 μm and from 6 ∼ 16 μm for the samples with and without Nd210, respectively [23].…”
Section: Resultssupporting
confidence: 63%
“…We can see that the particle size of trapped Nd422 particles (dark color) ranges from 1 ∼ 9 μm and from 1 ∼ 15 μm for the samples with and without Nd242, respectively, indicating that the sizes of the Nd422 particles were reduced due to the addition of Nd242. A commensurate phenomenon of reduction in size of LRE211 was also reported for LRE123 bulks with the addition of Barich phases, e.g., LRE210 or LRE242 [18,[20][21][22][23]. Specifically, the particle size of Nd422 ranged from 1 ∼ 12 μm and from 6 ∼ 16 μm for the samples with and without Nd210, respectively [23].…”
Section: Resultssupporting
confidence: 63%
“…The oxygen‐controlled melt‐textured growth method, which uses low during the fabrication of an (LRE)BCO superconductor, was found to be the most effective way to improve the superconducting properties of an (LRE)BCO bulk by suppressing an LRE/Ba substitution 20 . Different methods, such as a high crystallization rate 21 and postannealing in Ar, 22 using Ba‐rich precursors, 23 etc., have been developed to suppress the extent of LRE/Ba substitution during melt processing of (LRE)BCO bulks in an air atmosphere. However, in contrast to Sm and Nd systems, the transition temperature of the Gd system bulk superconductors did not appear to decrease considerably when they were fabricated in air 24 .…”
Section: Study Of the Superconducting Properties Of Gdbco Singlementioning
confidence: 99%
“…On the basis of the phase diagram in figure 1, doping BaCuO 2−x shifts the nominal composition towards a Ba-rich direction. It has been proved that a Ba-rich composition dramatically narrows the range of RE-Ba substitution [5][6][7]. Moreover, it is worth noting that excess BaCuO 2−x leads to a decrease in T c .…”
Section: Suppression Of Re-ba Substitutionmentioning
confidence: 99%
“…In previous studies, RE 2 BaO 4 addition was chosen to suppress the RE-Ba substitution during the melt growth in air [5,6]. Indeed this induces a Ba-rich composition, which is similar to using Ba-rich Nd 4+2x Ba 2+2x Cu 3−x O 10−y in the synthesis of high-T c NdBa 2 Cu 3 O 7−δ in air [7].…”
Section: Introductionmentioning
confidence: 99%