Failure characteristics of self-compacting concretes made with recycled aggregates

Gesoğlu, Mehmet; Güneyisi, Erhan; Öz, Hatice Öznur; Taha, Ihsan; Yasemin, Mehmet Taner

doi:10.1016/j.conbuildmat.2015.08.036

Cited by 112 publications

(43 citation statements)

References 31 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Fakitsas et al regarded that the reason for these findings was due to the water absorption of the RA when it was submerged in water. Ranjbar et al and Gesoglu et al reported high water absorption characteristics of RAs compared with natural aggregates. As a result, the saturating treatment and a maximum replacement at 30% for RA were suggested in SCC.…”

Section: Introductionmentioning

confidence: 97%

Experimental analysis of fiber‐reinforced recycled aggregate self‐compacting concrete using waste recycled concrete aggregates, polypropylene, and steel fibers

Aslani

Hou

Nejadi

et al. 2019

Structural Concrete

View full text Add to dashboard Cite

Self-compacting concrete (SCC) is a cementitious composite which serves complex formworks without mechanical vibrations with superior deformability and high resistance to segregation. Besides, the recycled aggregate concrete (RAC) is also developing rapidly and along with the ever-increasing sustainable demand for infrastructure. The combination of the fibers, RAC, and SCC may create advantages for the construction industry. In this study, the polypropylene (PP) fiber at 0.1, 0.15, 0.2, and 0.25% volume fractions and steel fibers at 0.25, 0.5, 0.75, and 1% volume fractions are introduced into fiber-reinforced recycled aggregate selfcompacting concrete (FR-RASCC). Both fresh property and hardened mechanical performance, comprising compressive and tensile strengths and modulus of elasticity are analyzed. The fibers validate the optimal 0.1% volume fraction for PP fiber and 0.75% volume fraction for steel fiber. In addition, the results are proved to enhance the mechanical properties and reduce cracking despite the negative impact on the fresh property. Moreover, the experimental outcomes are compared with previous researches to establish the linear model, demonstrating the relationship between fiber fraction and the mechanical properties. K E Y W O R D Sfiber-reinforced recycled aggregate self-compacting concrete, polypropylene fibers, recycled aggregate concrete, self-compacting concrete, steel fibers

show abstract

Section: Introductionmentioning

confidence: 97%

Experimental analysis of fiber‐reinforced recycled aggregate self‐compacting concrete using waste recycled concrete aggregates, polypropylene, and steel fibers

Aslani

Hou

Nejadi

et al. 2019

Structural Concrete

View full text Add to dashboard Cite

show abstract

“…For years now researchers have been studying the impact of the amount of added crushed recycled aggregate on concrete strength. Results compiled and presented in studies [14,21,[27][28][29][30][31][32] do not provide an unequivocal assessment of the impact exerted by cullet on concrete strength. Researchers argue that as the contents of recyclate are increased, the compressive strength of concrete tends to drop.…”

Section: Introductionmentioning

confidence: 99%

Effect of High Temperatures on the Impact Strength of Concrete Based on Recycled Aggregate Made of Heat-Resistant Cullet

2020

View full text Add to dashboard Cite

The article presents results obtained during testing of concrete based on CEM I 42.5R Portland cement, fine and coarse aggregate, glass, volatile ash, and superplastifier. The concrete mixture was modified using filler consisting of bromosilicate heat resistant cullet. Recycled aggregate was added to the batch. Samples for the need of testing were produced as (100 × 100 × 100) mm cubes. Before commencing proper tests, samples have been heated within the temperature range of 20–800 °C. Tests carried out during the proper testing procedure included tests of compressive strength, elevated temperature, impact strength, as well as macroscopic tests of the contact area. The obtained test results have provided proof of there being a possibility of producing special concrete, modified by products obtained from heat resistant cullet. This type of is generally characterized by satisfactory performance parameters. The average compressive strength for concrete modified by a 10% of heat resistant cullet was determined as 43.6 MPa and 48.3 MPa respectively after 28 and 180 days of curing.

show abstract

“…Nesse sentido, a relação resistência à tração/compressão dos concretos com agregados reciclados do presente estudo variou entre 9,70% à 10,58%, e o concreto referência apresentou relação igual a 11,21%. De mesmo modo, [26,28] notaram diminuição na resistência à tração em concretos autoadensáveis produzidos com agregados reciclados. O módulo de elasticidade do concreto é dependente do módulo de elasticidade dos agregados utilizados.…”

Section: Figuraunclassified

“…No entanto, não foi encontrada uma relação clara entre o percentual de incorporação e a redução desta propriedade das composições estudadas. [28] relataram diminuição do módulo de elasticidade, entre 13,12% a 18,42%, dos concretos autoadensáveis produzidos com emprego total de agregados graúdos reciclados. E semelhantamente, [29] observou a redução de 13,71% desta propriedade em composições onde houve substituição do agregado graúdo natural pelo reciclado, na proporção de 20%.…”

Section: Módulo De Elasticidadeunclassified

Efeito dos agregados graúdos reciclados nas propriedades de concretos autoadensáveis dosados por empacotamento de partículas

Cavaliere

Campos²,

Barbosa

et al. 2018

Libro De Comunicaciones / Livro Das Comunicações

View full text Add to dashboard Cite

RESUMOA construção civil é responsável por significativos impactos ambientais, uma vez que é expressiva consumidora de recursos naturais e grande geradora de resíduos sólidos. A utilização de agregados reciclados pode ser uma alternativa para a mitigação de tais impactos. Por essa razão, o objetivo desse trabalho foi analisar o comportamento, nos estados fresco e endurecido, de concretos autoadensáveis (CAA) produzidos com agregados graúdos reciclados e dosados por meio do conceito de empacotamento de partículas. Foram analisadas quatro composições de CAA, sendo que a primeira empregou apenas agregados naturais, e serviu de referência para este estudo. Nas demais misturas foram utilizados agregados graúdos reciclados de resíduos de construção e demolição em substituição à brita natural, em teores de 20, 50 e 100%, em massa. Os resultados obtidos demonstraram que todas as composições apresentaram desempenho satisfatório no estado fresco, porém, verificou-se que as propriedades mecânicas decresceram consoante o aumento no teor de agregado reciclado. PALAVRAS-CHAVE:concreto autoadensável; agregados reciclados; empacotamento de partículas; resíduos de construção e demolição; sustentabilidade. 1.-CONSIDERAÇÕES INICIAISO setor da construção civil consome elevada quantidade de recursos naturais, e por consequência, torna-se um expressivo gerador de resíduos de construção e demolição (RCD) [1]. Tais resíduos são diversas vezes descartados em locais impróprios, impactando significantemente o meio ambiente [2].Diante desse cenário, o controle dos resíduos de RCD minimiza tanto o consumo de recursos minerais, como pode ser considerado uma alternativa viável e ecológica para a 147

show abstract

Failure characteristics of self-compacting concretes made with recycled aggregates

Cited by 112 publications

References 31 publications

Experimental analysis of fiber‐reinforced recycled aggregate self‐compacting concrete using waste recycled concrete aggregates, polypropylene, and steel fibers

Experimental analysis of fiber‐reinforced recycled aggregate self‐compacting concrete using waste recycled concrete aggregates, polypropylene, and steel fibers

Effect of High Temperatures on the Impact Strength of Concrete Based on Recycled Aggregate Made of Heat-Resistant Cullet

Efeito dos agregados graúdos reciclados nas propriedades de concretos autoadensáveis dosados por empacotamento de partículas

Contact Info

Product

Resources

About