Failure of Lithium-Ion Batteries Accelerated by Gravity

Abstract

The safety concerns surrounding lithium-ion batteries (LIBs) have garnered increasing attention due to their potential to endanger lives and incur significant financial losses. However, the origins of battery failures are diverse, presenting significant challenges in developing safety measures to mitigate accidental catastrophes. In this study, the aging mechanism of LiNi 0.5 Co 0.2 Mn 0.3 O 2 ||graphitebased cylindrical 18,650 LIBs stored at room temperature for two years was investigated. It was found that an uneven distribution of electrolytes can be caused by gravity, leading to temperature variations within the battery. Specifically, it was observed that the temperature at the top of the battery was approximately −0.89 °C higher than at the bottom, correlating with an increase in partial internal resistance. Additionally, upon disassembly and analysis of spent batteries, the most significant damage to electrode materials at the top of the battery was observed. These findings suggest that gravity-induced electrolyte insufficiency exacerbates side reactions, particularly at the top of the battery. This study offers a unique perspective on the safety concerns associated with high-energydensity batteries in long-term and large-scale applications.