Fatigue Performance of Aged SAC-Bi Solder Joint under Varying Stress Cycling

Jian, Minghong; Vyas, Palash Pranav; Wei, Xin; Belhadi, Mohamed El Amine; Hamasha, Sa’d; Suhling, Jeff; Lall, Pradeep

doi:10.1109/itherm51669.2021.9503294

Cited by 7 publications

(1 citation statement)

References 39 publications

Supporting

Mentioning

Contrasting

Order By: Relevance

“…Following the reflow process, copper from the pad dissolved into the bulk solder and developed an intermetallic compound (IMC) at the interface. The IMC layer ensures that the solder and the substrate have strong metallurgical bonding [ 3 , 4 ]. This IMC layer has continued to develop during the reflow operation, which was detrimental to the strength of the joint owing to its brittle nature.…”

Section: Introductionmentioning

confidence: 99%

The Effect of Micro-Alloying and Surface Finishes on the Thermal Cycling Reliability of Doped SAC Solder Alloys

et al. 2022

Self Cite

View full text Add to dashboard Cite

The surface finish (SF) becomes a part of the solder joint during assembly and improves the component’s reliability. Furthermore, the SF influences the solder joint’s reliability by affecting the thickness of the intermetallic compound (IMC) layer at the solder interface and copper pads. In this experiment, five different alloys are used and compared with the SAC305 alloy, two of which, Innolot and SAC-Bi, are bi-based solder alloys. This study includes three common SFs: electroless nickel immersion gold (ENIG), immersion silver (ImAg), and organic solderability preserve (OSP). The performance of three surface finishes is examined in terms of component characteristic life. All of the boards were isothermally aged for twelve months at 125 °C. The boards were then exposed to 5000 cycles of thermal cycling at temperatures ranging from −40–+125 °C. Most of the current research considers only one or two factors affecting the reliability of the electronic package. This study combines the effect of multiple factors, including solder paste content, SF, isothermal aging, and thermal cycling, to ensure that the test conditions represent real-world applications. In addition, the electronics packages are assembled using commercialized alloys. The current study focuses on a high-performance alloy already present in the electronic market. The failure data were analyzed statistically using the Weibull distribution and design of experiments (DOE) analysis of variance (ANOVA) techniques. The findings reveal that the micro and uniformly distributed precipitates in solder microstructures are critical for high-reliability solder joints. Re-crystallization of the thermally cycled solder joints promotes the local formation of numerous new grains in stress-concentrated zones. As the fracture spreads along these grain boundaries and eventually fails, these new grains participate in crack propagation. Aging significantly worsens this situation. Finally, although the ENIG surface finish with its Ni layer outperforms other SFs, this does not imply that ENIG is more reliable in all solder paste/sphere/finish combinations.

show abstract

Section: Introductionmentioning

confidence: 99%