Formation of a Surface Charged Microarc Coatings Modified by Boehmite Nanoparticles

Abstract

Investigations of microarc calcium phosphate (CaP) boehmite-containing biocoatings on the pure titanium (Ti) alloy were presented. There were discovered relationships of coating properties (morphology, elemental and phase composition, zeta-potential, wettability) on the boehmite deposition parameters. A variation of the modification parameters of boehmite nanoparticles deposition allowed producing hydrophilic boehmite-containing CaP coatings with the roughness of 2.2-3.1 μm and nanoscale morphology. The influence of boehmite nanoparticles on the surface zeta-potential of the coating was found.

Formirovanie i svoystva kaltsiyfosfatnykh mikrodugovykh pokrytiy s nanochastitsami AlOOH

“…В экспериментах использовали подложки размерами 10×10×1 мм 3 из технически чистого титана марки ВТ1-0. КФ покрытие формировали методом МДО на установке «MicroArc-3.0» в электролите на основе водного раствора ортофосфорной кислоты, карбоната кальция и гидроксиапатита [5]. Морфологию поверхности КФ покрытий исследовали методом растровой электронной микроскопии (РЭМ) на микроскопе «LEO EVO-50» (ЦКП Нанотех, Томск).…”

“…Наночастицы бемита осаждали на готовые КФ покрытия в результате реакции гидролиза с предварительной ультразвуковой (УЗ) обработкой порошка алюмонитридной композиции AlN для его диспергирования. Длительность предварительной УЗ обработки составила 60 мин [5].…”