Formation of bulk (Zr, Ti)-based metallic glasses

A deep eutectic point in quaternary Zr–Ti–Ni–Cu system and bulk metallic glass formation near the eutectic point

“…He reported the quaternary deep eutectic Zr 54 Ti 23 The correlation between BMGs and their equilibrium intermetallic phases was studied by Molokanov et al [35]. They found that the equilibrium phases of reported multi-component BMGs are always composed of multiple ordered intermetallics based on eutectic systems.…”

Variation of microstructure of Zr60Al15Ni25 bulk amorphous alloy during rolling at room temperature

“…However, they are metastable in thermal dynamics [1,2]. Crystallization will occur due to heating or plastic deformation, resulting in the change of microstructure of alloys.…”

On the synthesis of Zr-based bulk amorphous alloys from glass-forming compounds and elemental powders

“…The ratio between the total volume fractions of binary and ternary crystal phases is close to 3:2 in these alloys [11]. A similar ratio of ZrNiTi ternary Laves phase to binary phases was found to be favorable for a sharp increase of the amorphous layer thickness in rapid-quenched alloys of Zr-Ni-Ti [12].…”