Freeze-thaw durability of recycled concrete containing ceramic aggregate

Medina, César; Rojas, M.I. Sánchez de; Frías, Moisés

doi:10.1016/j.jclepro.2012.08.042

Cited by 153 publications

(62 citation statements)

References 33 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Upon completion of 300 freeze-thaw cycles, the modulus of elasticity, tensile and compressive strength was measured on each specimen. In accordance with the ASTM C 666 standard (28) the relative dynamic modulus of elasticity (RDME) was calculated [1]:…”

Section: Freezing-thawing Testsmentioning

confidence: 99%

See 1 more Smart Citation

The influence of the curing conditions of concrete on durability after freeze-thaw accelerated testing

Al‐Assadi¹,

Casati²,

Gálvez³

et al. 2015

Mater. construcc.

View full text Add to dashboard Cite

This work relates the curing conditions of concrete with the damage caused by rapid freeze-thaw cycles (ASTM C 666). The "potential" durability of concrete after testing is also studied. In countries with a continental climate, the curing of concrete in summer is performed under high-temperature and low-humidity conditions, and during the winter the concrete undergoes freezing and thawing. This paper shows the experimental results of the behaviour of concrete specimens cured under climatic summer conditions and then subjected to freeze-thaw cycles. Curing of the specimens includes conditions of good and bad practice in relation to wetting and protection of the concrete. Mechanical properties, cement hydration, volume and pore sizes, oxygen permeability, chloride diffusion and water penetration under pressure tests of the concrete are assessed. These tests were performed before and after the application of the freeze-thaw cycles. Statistical analysis of the correlation among variables is also included. RESUMEN: Influencia de las condiciones de curado del hormigón en su durabilidad tras los ensayos acelerados de ciclos hielo-deshielo.Este trabajo relaciona las condiciones de curado del hormigón con los daños causados por ciclos hielo-deshielo (ASTM C 666). Estudia la durabilidad "potencial" del hormigón dañado por este ensayo. En países con clima continental, el curado del hormigón en verano se realiza con alta temperatura y baja humedad, y durante el invierno sufre condiciones de hielo-deshielo. Se presentan los resultados experimentales de probetas de hormigón curadas bajo condiciones climáticas del verano y luego sometidas a ciclos hielodeshielo. El curado de las probetas incluye condiciones de buenas y malas prácticas en relación con el curado del hormigón. Se miden las propiedades mecánicas, grado de hidratación, volumen de poros y distribución de tamaños, permeabilidad al oxígeno, penetración de agua bajo presión y coeficiente de difusión de cloruros antes y después de la aplicación de los ciclos de hielo-deshielo. Se incluye un estudio estadístico para analizar la correlación entre las variables.

show abstract

Section: Freezing-thawing Testsmentioning

confidence: 99%

“…The number of publications dealing with frost durability is extensive and this work does not seek to summarise all the contributions to this vast and complex subject (1)(2)(3)(4). Concrete behaves well even under adverse weather conditions if it has been adequately designed, cast and cured.…”

Section: Introductionmentioning

confidence: 99%

The influence of the curing conditions of concrete on durability after freeze-thaw accelerated testing

Al‐Assadi¹,

Casati²,

Gálvez³

et al. 2015

Mater. construcc.

View full text Add to dashboard Cite

show abstract

“…In a study carried out by Medina et al [13], it was found that the freeze-thaw durability of concrete made with 20-25% ceramic aggregate obtained from industry waste was better than that of conventional concrete after 56 freezethaw cycles. This better performance was due to the high mechanical quality of recycled concrete and the intrinsic properties of the new aggregate.…”

Section: Introductionmentioning

confidence: 99%

Compressive Strength Study on the Freeze-thaw Resistance of Recycled Aggregate Concrete Members

Niu¹,

Wang²,

Zhang³

et al. 2017

TOCIEJ

View full text Add to dashboard Cite

Introduction:Freeze-thaw resistance of recycled aggregate concrete with partial or total replacement of recycled aggregate compared with that of natural aggregate concrete was investigated in this paper. Method:Ninety specimens were fabricated to study the influence of different recycled aggregate replacement ratios on the surface scaling, mass loss, and residual compressive strength after 100 freeze-thaw cycles. Results:The experiment results indicate that the type of recycled aggregate and its replacement ratio have significant effects on the freezethaw performance. The cubic compressive strength of recycled aggregate concrete is overall slightly lower than that of normal concrete. After 100 freeze-thaw cycles, the compressive strength decreases and the reduction extent increases with increasing replacement rate of recycled aggregate. The surface scaling of reinforced recycled concrete prisms tends to be more severe with the increase of freeze-thaw cycles. Conclusion:Furthermore, a notable rise in mass loss and the bearing capacity loss is also found as the substitution ratio increases. Under the same replacement rate, recycled fine aggregate causes more negative effects on the freeze-thaw resistance than recycled coarse aggregate.

show abstract

“…Topçu y Canbaz [15] y Adamson et al [16] alcanzaron un aumento de la resistencia frente a ciclos hielo-deshielo cuando utilizaban tejas y ladrillos en sustituciones totales o parciales de los áridos naturales. Medina et al [17] registraron degradaciones de material similares para hormigones convencionales y para sustituciones del 20 y 25%. Topçu y Sengel [18] y Bazaz y Khayati [19] obtuvieron leves disminuciones de resistencia cuando incorporaban ladrillo triturado.…”

Section: -Introducciónunclassified

Resistencia de los hormigones elaborados con árido reciclado frente a ciclos de hielo-deshielo

Juan-Valdés

Rodríguez-Robles

García-González

et al. 2018

Libro De Comunicaciones / Livro Das Comunicações

View full text Add to dashboard Cite

RESUMENLos prometedores resultados alcanzados por los hormigones que incorporan áridos reciclados procedentes de hormigón en el sector de los pavimentos, han fomentado el interés por aumentar el espectro de materiales susceptibles de ser reciclados. Atendiendo al significativo volumen que supone en países como España y Portugal la fracción cerámica del total de los residuos de construcción y demolición, este estudio analiza el comportamiento de los hormigones que incorporan áridos reciclados mixtos y cerámicos frente a ciclos de hielo-deshielo. Para ello se elaboran 3 tipos de hormigón: un hormigón convencional con árido 100% natural, un hormigón reciclado donde el 50% del árido grueso natural es sustituido por árido reciclado mixto, y otro hormigón reciclado, donde el porcentaje de sustitución se mantiene en 50%, pero se utiliza árido reciclado cerámico. Los resultados alcanzados demuestran que las caras moldeadas de los hormigones reciclados mantienen los niveles de resistencia a hielo-deshielo experimentados por el hormigón convencional cuando el porcentaje de material cerámico es bajo, y superan dichos niveles cuando el porcentaje de cerámica aumenta. En las superficies enrasadas, la presencia de árido reciclado supone una pérdida de resistencia a los ciclos de hielo-deshielo, siendo menos intensa esta pérdida cuanto mayor es el contenido cerámico. PALABRAS CLAVE:Hormigón reciclado, hielo-deshielo, sales descongelantes. 1.-INTRODUCCIÓNEl sector de los pavimentos es una de las aplicaciones del hormigón donde mejor aceptación ha experimentado la utilización de áridos reciclados. Centrándose principalmente en la incorporación de áridos reciclados procedentes hormigón en su totalidad, debido a que se trata de un material inerte y con un gran potencial de reutilización. Los prometedores resultados alcanzados por esta aplicación han fomentado el interés por aumentar el espectro de materiales susceptibles de ser reciclados. Teniendo en cuenta el significativo volumen que supone en países como España y Portugal la fracción [21] afirmaron que el uso de áridos reciclados con contenidos elevados de material cerámico mejoraba la durabilidad de los hormigones elaborados. Por lo tanto, resulta de gran interés analizar el comportamiento durable de los hormigones elaborados con un contenido significativo de fracción cerámica reciclada como árido grueso. 2.-MATERIAL Y MÉTODOSPara la elaboración de las muestras de hormigón se ha empleado cemento tipo CEM III/B 42.5 N SR LH LA, agua de grifo y áridos naturales silíceos. Como árido reciclado se emplean dos muestras de material procedentes de plantas de gestión de residuos de construcción y demolición españolas. En la Tabla 1 se pueden observar los distintos componentes que integran la muestra ARM (procedente de la empresa madrileña TEC-REC) y la muestra ARC (suministrada por la empresa Bierzo Recicla con localización en Castilla y León), determinados según la norma EN 933-11/AC (2009) El comportamiento de los hormigones frente a los ciclos hielo-deshielo en combinación con el ...

show abstract

Freeze-thaw durability of recycled concrete containing ceramic aggregate

Cited by 153 publications

References 33 publications

The influence of the curing conditions of concrete on durability after freeze-thaw accelerated testing

The influence of the curing conditions of concrete on durability after freeze-thaw accelerated testing

Compressive Strength Study on the Freeze-thaw Resistance of Recycled Aggregate Concrete Members

Resistencia de los hormigones elaborados con árido reciclado frente a ciclos de hielo-deshielo

Contact Info

Product

Resources

About