Good combination of strength and mechanical isotropy in AA6082 alloy processed by high temperature intermediate annealing

Liu, Shichao; Xu, Guofu; Jin, Jialin; Li, Yao; Peng, Xiaomin

doi:10.1016/j.jallcom.2022.166229

Cited by 6 publications

(1 citation statement)

References 48 publications

Supporting

Mentioning

Contrasting

Order By: Relevance

“…As one of the most potential materials in recent decades, aluminum alloy has the advantages of high specific strength, low density, and convenient recycling [1][2][3]. Among them, 6000 series aluminum alloys also demonstrates preferable forming performance, excellent processing properties and satisfactory corrosion resistance [4].…”

Section: Introductionmentioning

confidence: 99%

Mechanical Properties and Microstructural Evolution of 6082 Aluminum Alloy with Different Heat Treatment Methods

Xia,

Ye,

Qiu

et al. 2024

Coatings

View full text Add to dashboard Cite

The influence of solid solution treatment (SST), artificial aging treatment (AAT), and deep cryogenic-aging treatment (DCAT) on the mechanical properties and microstructure evolution of 6082 aluminum alloy was investigated. The tensile test was performed to obtain the true stress–strain curves through an electronic universal testing machine. The results show that the yield strengths of the SST specimens in all three directions are the lowest, of less than 200 MPa. In addition, the maximum elongation of the SST specimen is over 16% and the value of in-plane anisotropy (IPA) is 5.40%. For the AAT specimen, the yield strengths of the AAT alloy in three directions have distinct improvements, which are beyond 340 MPa. However, the maximum elongation and the IPA were evidently reduced. The yield strength and elongation of the DCAT alloy exhibit a slight enhancement compared with those in the AAT condition, and the corresponding IPA is 0.61%. The studied alloy specimens in all conditions exhibit ductile fracture. The DCAT alloy has the highest density of precipitates with the smallest size. Therefore, the dislocation pinning effect of the DCAT specimens are the strongest, which exhibit the highest yield strength accordingly. In addition, the uniformly distributed precipitates in the matrix with a large ratio of long and short axes can suppress the anisotropy caused by elongated grains.

show abstract