Growth Law For Peritectic Phases Formation In The Zinc Coating

Abstract

Some experiments dealing with the isothermal hot dip galvanizing were carried out. The (Zn) -coating settled on the Armco-iron substrate were examined after arresting the solidification for different periods of time. The measurement of the thickness of each sub-layer in the coating were performed due to the SEM -analysis. The zinc segregation on the cross-section of the studied sub-layers were also determined by the EDS technique. The growth laws are formulated mathematically for each of the observed sub-layer. The mechanism of the sub-layer formation is also analysed due to the observation of the birth/nucleation of the phases in the sub-layers and the effect of flux onto the sub-layers morphology formation. The appearance of each phase is referred to the Fe-Zn diagram for stable equilibrium according to which these phases are the products of the adequate peritectic transformation.Keywords: (Zn) -coating; zinc segregation; growth law; crystallization of peritectic phases Przeprowadzono eksperymenty izotermicznego cynkowania zanurzeniowego. Powłoka (Zn) osadzona na żelazie Armco poddana została badaniom po zatrzymaniu krystalizacji dla różnych czasów trwania cynkowania. Dokonano pomiarów grubości każdej z podwarstw powłoki dzięki analizie SEM. Segregacja cynku na przekroju badanych podwarstw również została określona dzięki pomiarom przy użyciu techniki EDS. Sformułowane są matematycznie prawa wzrostu dla każdej z analizowanych podwarstw. Analizowany jest również mechanizm kształtowania podwarstw dzięki obserwacjom narodzin/zarodkowania poszczególnych faz w podwarstwach oraz dzięki analizie oddziaływania topnika na morfologię podwarstw. Formowanie każdej z faz jest odniesione do diagramu równowagowego Fe-Zn zgodnie z którym fazy te są produktami odpowiednich reakcji perytektycznych.