Hyper‐crosslinked sorbents for hemoperfusion

Abstract

Pore structure changes of swelling sorbents, which were obtained from styrene and divinylbenzene (DVB) by additional crosslinking with a,a'-dichloro-p-xylene in the presence of tin chloride catalyst and in dichloroethane solution, were examined. It was found that the amount of dichloroxylene influences the swelling decrease and the increase of sorption ability of sorbents for chemical compounds with low molecular weight. Hemocornpatibility was imparted to the sorbent and it was useful for hemoperfusion when a small amount of sulfonyl groups (about 0.2 mmol/g) had been introduced. ZUSAMMENFASSUNG:Veranderungen der Porenstruktur von quellbaren Sorbentien, hergestellt durch zusatzliche Vernetzung von Styrol-Divinylbenzol-Copolymeren mit a,a'-Dichlorxylol in Gegenwart eines Zinnkatalysators in Dichlorethan, wurden untersucht. Der Gehalt an Dichlorxylol beeinfluat die Abnahme der Quellbarkeit und die Zunahme der Sorptionsfahigkeit fur niedermolekulare Verbindungen. Die Sorbentien waren hamokompatibel und konnten nach Einfuhren geringer Mengen Sulfonylgruppen (ca. 0.2 mmol/g) zur Hamoperfusion eingesetzt werden.