Influence of Granulation of Powder Charge of Titanium-Boron on Regularities of Self-Propogating High-Temperature Synthesis of Porous Materials

Abstract

The results of studies of fabrication of porous titanium boride TiB by self-propagating high-temperature synthesis (SHS) using ordinary (not granular) and granular initial powder charge titanium-boron are presented. The influence of the amount of titanium in the charge, the granule size and the pressure of compaction of the charge on the structure, porosity, phase composition and compression strength of the resulting porous materials is described. The results of studies were obtained with the use of the scanning electron microscope, diffractometer and universal testing machine.

Synthesis of Porous Composite Material with the Combustion of Titanium and Boron Powders and Nickel-Clad Aluminum Granules

“…Получение тугоплавких материалов методом самораспространяющегося высокотемпературного синтеза (СВС) обладает целым рядом преимуществ, так как позволяет не только синтезировать в одну технологическую стадию продукт заданного химического состава, но и управлять его макрои микроструктурой за счет простого изменения характеристик компонентов исходных порошковых смесей [1][2][3][4]. Использование порошков с конгломерированными, плакированными или композитными частицами, в которых компоненты определенным образом пространственно распределены, дает дополнительные возможности по управлению структурой продукта, позволяя получать развитую разномасштабную пористость и сложное распределение структурных элементов [3][4][5][6][7]. При этом возможно получение пористого СВС-продукта с композиционной структурой, в котором фазы и поры расположены упорядоченно за счет применения специальных методов формования реакционной смеси, обеспечивающих упорядоченное расположение ее частиц в объеме исходных заготовок [4][5][6][7].…”