Influence of hydrothermal conditions on the mechanical properties of hybrid composite pipes

Abstract

Composite materials are becoming widespread in many sectors today, especially in the defence and space industry. Composite materials can be exposed to significant temperature changes and various environmental conditions depending on their usage areas. Therefore, composite materials with high resistance to high temperatures and harsh environmental conditions are being studied today. In this study, four types of 6-layer composite pipes with glass/glass/glass, basalt/basalt/basalt, glass/basalt/glass and basalt/glass/basalt stacking sequences were fabricated with filament wound method. In order to simulate the behavior of composite materials under environmental conditions, specimens were subjected to hydrothermal aging in pure water at 70°C for three different periods of 500, 1000 and 1500 hours. During the aging process, the mass changes of the pipes were measured regularly, and the water absorption behavior was determined with reference to ASTM D5229 standard. Hardness tests were carried out with Rockwell hardness tester based on ASTM D785 standard. As a result of the study, it was determined that the mechanical performance of hybrid specimens was higher than that of non-hybrid specimens. It was observed that the hydrothermal aging process caused a loss of mechanical strength in all specimens. It was concluded that the hybrid composite specimen with basalt/glass/basalt stacking order had the highest resistance to hydrothermal aging.