Influence of Oversized Dowel Space Preparation on the Bond Strengths of FRC Posts

Abstract

SUMMARYThis study compared the bond strengths of fiberreinforced composite (FRC) posts luted into oversized dowel spaces with FRC posts luted into precisely fitting dowel spaces using five different resin cements or build-up composites. The hypotheses examined were that bond strength does not present vast variations according to the width of the gap between the root canal and post and that bond strength increases for FRC posts luted with build-up composites compared with FRC posts luted with resin cements. Dowel space preparations (ER post-restoring system, 12 mm in length) were performed on 100 human anterior teeth up to ISO 90 and ISO 110 of 50 roots each. FRC posts, all ISO size 90, were inserted into the precisely fitting as well as into the oversized dowel spaces (n=10) using five composite materials (Calibra, Multicore Flow, Rely X Unicem; resin cements and Build-It, Rebilda DC; build-up composites). The manufacturers' instructions of the composite materials were strictly followed except for Rebilda DC, which was used with Adhese for dentin bonding. Following water storage (37°C, 24 hours) and thermocycling (5000 cycles, 5°C-55°C, 30 seconds) tensile strength testing was performed and fracture modes were assessed using SEM.

Pull-out тест и ефектoт од употребата на различни видови цементи и надградбени системи врз ендондонски третирани заби

“…Иако во прегледаната литература се достапни малку информации за улогата на цементната дебелина на смолестите цементи за ретенција на надградбените системи, сепак некои студии имаат објавено пониски сили на притискање или извлекување при зголемување на http://www.id-press.eu/mmej/ дебелината на цемент [10,11]. Сепак, овие литeратурни податоци се спротивни од други студии кои укажуваат дека зголемување на цементната дебелина резултира со зголемување на јачината од извлекување [12].…”

“…Од друга страна еугенол полнењата, остатоците од гутаперка од претходно изведените кондензационите процедури, Ni-Тi ротационите канални инструменти покажуваат негативно влијание врз атхезијата на колчињата [18,19].…”

In vitro evaluation of the shear bond strength between fiber posts and methacrylate or silorane based composite resins

“…However the fracture patterns are usually about failures in adhesion between post and resin material, either composite or resin cement [3,28]. In that matter, different surface treatments have been described, such as silanization and application of an adhesive system [3,4,[28][29][30][31][32], to ensure the bond between the resin-based materials and FP. However, for the customized-post technique there are not enough studies to determine if the adhesive use in the preparation of FP surface is actually required [33,34].…”

“…In some clinical situations, the space between the FP and the walls of the root canal may be too wide due to the root canal anatomy and/or treatment [1,3,4]. As the thickness of the composite resin cement directly influences the FP adaptation and consequently the bond strength [3,4], thinner cement layers are desirable for better mechanical properties [5,6].…”

Estudo, in vitro, da influência da técnica e do aparelho de fotopolimerização na resistência de união de pinos intra-radiculares

“…Isso pode ter ocorrido devido à alta compatibilidade química do adesivo Scotch Bond Multi Uso com o cimento resinoso Rely X . Em outro estudo de retenção de pinos, Schmage et al (2009), também obtiveram alguns resultados em que a fratura ocorreu na interface pino/cimento. Segundo o autor, isso ocorreu devido à alta adesão obtida pelo adesivo dual na dentina, fazendo com quem a interface pino/cimento fraturasse em primeiro.…”