Influence of Resin Content and Density on Water Resistance of Bamboo Scrimber Composite from a Bonding Interface Structure Perspective

Abstract

As a new type of green environmental protection material for outdoor use, the water resistance of bamboo scrimber composite (BSC) is crucial—the primary reason for a decrease in water resistance being bonding interface failure. From a bonding interface structure perspective, the influence mechanism of the resin content and density on the water resistance of BSCs remains unknown. Therefore, in this study, BSCs were prepared using Moso bamboo and phenol-formaldehyde resin, and the changes in the macroscopic and microscopic bonding interfaces before and after 28-h water-resistance tests were observed and analyzed. The results showed that the water resistance of the BSC increased with increasing resin content, with higher thickness swelling rates (TSRs) observed at higher densities. Obvious cracks were found at the macroscopic interface after 28-h tests, with higher resin contents leading to fewer and smaller cracks. With increasing density, the longitudinal fissures due to defibering process decreased, having an effect on width swelling rates (WSRs). Furthermore, porosity measurements revealed changes in the microscopic bonding interface; the difference in porosity before and after testing (D-value) showed the same trend as water resistance. Generally, we conclude that the macroscopic and microscopic bonding interface structures are closely related to BSC water resistance.

Investigating the influence of sugarcane bagasse ash volume variation in glass fiber reinforced with epoxy resin matrix composite material

“…In polymer composite materials, mass per unit volume is a crucial parameter that defines their qualities. [26][27][28][29] The developed composite was weighed using a digital weighing scale and the volume was determined using a measuring cylinder. To conduct the test, distilled water was taken as the medium.…”