Influence of the Crystal-Chemical Structure in Calcium-Phosphate Nanocomposite on the Formation of Electrosurface and Acid-Basic Properties

Abstract

The single-phase modified nanostructured hydroxyapatites and biomimetic calcium-phosphate nanocomposite (BMHAP) doped by silicate and carbonate anions are synthesized by chemical precipitation in aqueous solutions. The chemical composition of the obtained samples is studied by energy dispersive X-ray spectroscopy using a scanning electron microscope. It is shown that the obtained molar ratios are close to the design values in all samples. The influence of different modifying ions in the crystal-chemical structure of hydroxyapatite (HAp) on the electrosurface properties of the synthesized products has been studied. Unmodified hydroxyapatite, silicate-substituted hydroxyapatite, and BMHAP particles are found to carry a negative charge in an aqueous suspension at pH = 7, while carbonate-substituted HAp particles had a positive charge. It is revealed that the introduction of silicate and carbonate anions into the HAp structure is accompanied by an increase in negative values of the zeta-potential from -1.05 to -4.29 mV. The change in the distribution of active centers on the surface of modified nanostructured hydroxyapatites is studied by the adsorption of acid-base indicators method with pKax in the range from -0.3 to +12.8. In contrast to stoichiometric hydroxyapatite, in BMHAP the neutral Bronsted centers prevails, and their concentration is 48.38 mmol-eq/g