Inhomogene Verformungserscheinungen bei Schwingbeanspruchung des Vergütungsstahls 42 CrMo 4

Abstract

lnhomogeneous Deformation Processes During Cyclic Loading of Quenched and Tempered Steel SAE 4140The cyclic deformation behavior of a normalized steel SAE 4140 in the loading range aa < Rcs is characterized by softening and hardening phcnomena. Cyclic softening processes are combined with inhomogeneous plastic deformations and the propagation of a fatigue Liidersband. The following hardening process occurs homogeneously.At stress amplitudes ua < q0 the quenched and tempered SAE 4140 worksoftens continuously until crack initiation. Plastic deformation processes are extremely inhomogeneous and are concentrated on small fatigue zones. The inhomogeneity increases with decreasing tempering temperatures und stress amplitudes.

Dauerschwingfestigkeit und zyklisches Werkstoffverhalten

“…Fatigue limit, aw, versus cyclic yield strength, Rho,*. Verformung uber der Prtiflange einer Probe inhomogen verteilt sein kann[8] bzw. die Dauerfestigkeitsgrenze rnit der Bildung von Mikrorissen in Verbindung gebracht wird, wobei diese Mikrorisse lokal auftreten, so daB eine mittlere makroskopische plastische Verformung, wie sie sich im zyklischen Versuch einstellt, keine Aussage uber die ortlich auftretenden Spannungskonzentrationen liefern kann.…”