Insights into the Deterioration Mechanism of Charging Ability during Calendar Aging and Cycling Aging of High-Voltage Co-Poor NCM Cathode-Graphite Full Battery

Abstract

Lithium-ion battery (LIB) has gained significant recognition for the power cell market owing to its impressive energy density and appealing cost benefit. Among various cathodes, a high-voltage cobalt-poor lithium nickel manganese cobalt oxide cathode (Co-poor NCM cathode) has been considered as a promising strategy to enhance its energy density. Despite these advantages, high-voltage Co-poor NCM cathode-graphite full battery usually suffers from poor rate performance. However, fast charging has been a key indicator for widespread application of power batteries. Although many efforts have been made to improve the charging performance of fresh batteries, few works investigate the charging ability during calendar aging and cycling aging of high-voltage Co-poor NCM cathode-graphite full battery. In this work, we found that the charging ability becomes worse during calendar aging and cycling aging. Results showed that the increasing charge transfer resistance from the cathode is the major obstacle to achieving fast charging during the aging process. To address the problem, high-voltage Al 2 O 3 -coated Co-poor NCM cathode successfully prepared via a simple atomic layer deposition (ALD) method has been developed to reduce the decay of charging performance during calendar aging and cycling aging. Al 2 O 3 -coated NCM cathode can effectively reduce the growth rate of the resistance of cathode, which is benefiting from the conversion of Al 2 O 3 into LiAlO 2 with high ionic conductivity and the restriction formation of rock salt phase. Benefiting from the decreased charge transfer resistance of the NCM cathode, the mismatch of the lithium-ion reaction kinetics is well alleviated, thus effectively reducing the polarization under fast charging. As a result, Al 2 O 3 -coated NCM cathode-graphite full battery shows the slow deterioration of charging performance during the aging process. This work provides a promising strategy for constructing fast-charging batteries during calendar aging and cycling aging.