Investigation of microstructural damage to eutectic carbides from scratch tests of a heat-treated Fe–Cr–W–Mo–V–C alloy

Abstract

Abstract:The characteristics of abrasive wear damage to the carbides and eutectic phases in a Fe-Cr-W-Mo-V-C alloy were systematically investigated using point scratch testing on heat-treated samples with preserved eutectic structures from a characteristic eutectic carbide formation temperature of 1240°C. A deep-etching method is applied to study the detailed morphologies of the eutectic carbides by optical microscopy (OM) and field emission scanning electron microscopy (FESEM). The types of the eutectic carbides was identified by X-ray diffraction (XRD) as V-rich eutectic MC and Mo-rich eutectic M 2 C. Single-pass scratch tests were carried out on polished and deep-etched surfaces of the specimens to investigate the micro-scale wear behavior of the eutectic carbides with and without protection by the matrix phase. It was found that, when a surrounding matrix is present, the micro-cracks initiate from the eutectic region during the scratch tests and slip-lines appear in scratched edges of the matrix phase. Without matrix protection as revealed in the deep etched samples, the main failure form is carbide dendrites break-off forming wear debris. The detailed differences in response and deformation mode of carbide microstructures with/without matrix support to single-point abrasion behavior are schematically depicted for main eutectic MC and M 2 C carbides under different loading conditions. Potential 2 improvement on wear performance through the composition design is also discussed based on the different fracture and wear behavior of V-rich eutectic MC and Mo-rich eutectic M 2 C identified