Leaching of Gold and Copper From Printed Circuit Boards Under the Alternating Current Action in Hydrochloric Acid Electrolytes

Self Cite

This paper presents the results of the leaching of metals from computer PCBs by electrochemical hydrochlorination using alternating current (AC) with an industrial frequency (50 Hz). Leaching was carried out with a disintegrator-crushed computer motherboard with a particle size (d) of <90 μm. In the course of the research, the leaching efficiency of metals including Fe, Sn, Mn, Al, Cu, Zn, Pb, Ni, Ti, Sb, Cr, Co and V was evaluated depending on process parameters, such as AC density, experiment duration, hydrochloric acid concentration in the electrolyte solution, solid/liquid ratio, electrolyte temperature, and the loading option of raw material (loading option 1 involving loading into the electrolyte solution, and loading option 2 involving loading into the filter containers attached to electrodes). The research results showed that AC superimposition significantly intensifies the leaching of metals. It was established that the complete leaching of metals including Al, Mn, Sn, Ti and Zn, under experimental conditions (loading option 2, CHCl = 6 mol·L−1, i = 0.80 A·cm−2, S/L = 8.6 g·L−1), is reached after 1.5 h, and that of Cu and Ni is reached after 2 h from the beginning of the experiment. At the same time, the degree of leaching of other metals after 2 h is Co-78.8%, Cr-84.4%, Sb-91.7%, Fe-98.9%, V-98.1% and Pb-5.1%. The paper also reports the results on the leaching of all abovementioned metals, as well as Ag and Pd, with disintegrator-crushed mixed computer PCBs with d < 90 μm and loading option 1.

Study of Metal Leaching from Printed Circuit Boards by Improved Electrochemical Hydrochlorination Technique Using Alternating Current

Serga

Žarkov

Shishkin

et al. 2023

Self Cite

Advanced Technologies in Bio/Hydrometallurgy for Recovery and Recycling of Metals

Ubaldini

2023

Investigation of the Impact of Electrochemical Hydrochlorination Process Parameters on the Efficiency of Noble (Au, Ag) and Base Metals Leaching from Computer Printed Circuit Boards

Serga,

Zarkov,

Shishkin

et al. 2024

Self Cite

The development of environmentally friendly and energy-saving processes for recycling electronic waste (e-waste) is still relevant today. The research presented in this work relates to hydrometallurgy, namely, the electrochemical leaching of metals from e-waste under the action of alternating current (AC) into hydrochloric acid solutions of electrolytes, and can be used for leaching both noble and non-ferrous metals from secondary raw materials. The main object of the study was disintegrator-crushed mixed computer PCBs metal-rich powders with a particle size (d) of <90 µm. The impact of such leaching process parameters as temperature (Tel) and composition of the electrolyte solution, AC density (i) on the electrodes, experiment duration (tex) while maintaining a constant electrolyte temperature (60 °C, 70 °C, and 80 °C) on the metal (Au, Ag, Cu, Al, Ni, Pb, Sn, Ti, Zn, and Fe) leaching efficiency has been studied. In addition, under similar experimental conditions, but without external control of Tel, the kinetics of metal leaching from raw material powders obtained via PCBs single and double crushing in a disintegrator has been also presented. Comparison of raw material powders obtained from different batches of the source material showed both the variability of its chemical composition and the different kinetics of Au and Ag leaching under the same experimental conditions. The optimal conditions for pretreatment of the raw material obtained by single crushing in a disintegrator (CHCl = 6 mol·L−1, i = 0.88 A·cm−2, tex = 1 h, solid-to-liquid ratio—8.6 g·L−1 and without external control of Tel) were determined. It has been shown that this electrochemical pretreatment is accompanied by transition of only base metals into the electrolyte solution, making it possible to significantly reduce their concentration in the final solution. Under pretreatment conditions, the following degree of metal leaching (RMe) has been established: RCu = 98.2%, RAl = 62.8%, RNi = 53.4%, RPb = 93.2%, RSn = 98.0%, RTi = 88.5%, RZn = 61.6%, and RFe = 78.8%. As a result of a subsequent two-hour electrochemical treatment of a solid residue, the degree of leaching of gold and silver was 73.6% and 86.7%, respectively. The presented results provide a broader understanding of the possibility of using the proposed electrochemical hydrochlorination method for noble and base metals leaching from waste PCBs. The novelty and practical value of this research is a validation of the developed technology in laboratory conditions using the real batch of the PCBs. This approach may also be useful to researchers involved in the recycling of other types of secondary raw materials.