Magnetism of amorphous Dy-Tb-Co-type films

Abstract

In this work a systematic study of magnetic properties of amorphous TbxCo100-x and DyxCo100-x films is presented. In a composition range 15 < x < 40 at. %, temperature dependencies of spontaneous magnetization in a temperature interval 5 – 300 K as well as low-temperature 5 K hysteresis loops in magnetic field up to ±70 kOe have been obtained. We demonstrated, that the experimental results can be interpreted in a framework of a model considering a variable sperimagnetic cone angle of rare earth atoms up to 150°. A series of Tb-Dy-Co films with a composition close to Laves phase has been obtained. We demonstrated that the variation of rare earth content with Co content fixed does not lead to a systematic lowering of magnetic hysteresis.

Temperature Stability of Crystalline Structure, Electro- and Magnetotransport Properties of Functional Nanostructures of Spin-Valve Type Ni/Dy/Co

“…Дедалі частіше дослідники звертають увагу на тонкоплівкові системи, в основі яких рідкоземельні (R) та перехідні феромагнетні (T) метали [2][3][4]. Такі системи характеризуються феромагнетним упорядкуванням [5][6][7]. Крім того, для тонких плівок рідкоземельних металів характерна сильна розмірна залежність кристалічної структури, що може змінюватися від аморфної до кристалічної [8], а аморфна структура плівок магнетних металів з неупорядкованим розташуванням атомів призводить до сильних змін їхніх магнетних характеристик.…”