Mathematical description of static recovery of type C–Mn–Mo–Nb–V microalloyed steel

Abstract

A new method of determining the softening ratio X was evaluated by comparing stress-strain curves over the yield point. A widely executed experimental program on the computer-controlled torsion plastometer allowed us to provide the mathematical description of the X-value as a function of the deformation temperature T and time t between deformations, temperature of austenitization T a , strain e and strain rate e of the previous pass, respectively. The picture in words refers to a microalloyed steel base of G-Mn-Mo-Nb-V which is recovered in the temperature range from 700 to 900 DC. Mathematische Beschreibung der statischen Erholung eines mikrolegierten e-Mn-Mo-Nb-V-Stahles. Eine neue Methode zurBestimmung der Erweichungsgeschwindigkeit X wurde entwickelt. Dabei werden Spannungs-Dehnungs-Kurven entlang der Streckgrenze verglichen. Ein breit angelegtes Versuchsprogramm auf dem computergesteuerten Torsionsplastometer errnoqllcht die mathematische Beschreibung des X-Wertes als Funktion der Umformtemperatur Tund der Zeit tzwischen den Umformungen, Austenitisierungstemperatur T a , Formiinderung e und Formiinderungsgeschwindigkeit e des vorangegangenen Stiches. Als Beispiel zur Veranschaulichung wird ein mikrolegierter G-Mn-Mo-Nb-V-Stahl herangezogen; der Temperaturbereich der Erholung lag hierbei zwischen 700 und 900 DC.

Avaliação Do Amaciamento Estático a Quente E a Morno De Um Aço Silicioso

“…Este método consiste em se aplicar, através de ensaios mecânicos de deformação a quente, dois passes sucessivos, normalmente com a mesma quantidade de deformação, geralmente baixa, inferior a 0,3. (3)(4)(5) Com isto, a restauração estática é avaliada em função do intervalo de tempo entre os dois passes.…”