Mechanical characterization of high volume fraction Al7075-Al2O3 composite fabricated by semisolid powder processing

Abstract

The mechanical properties and physical characteristics of aluminum alloy composites can be significantly improved by adding reinforcing phases. However, the high loading of the reinforcement phase in Al7075-Al2O3 composites has not been thoroughly studied. In this work, a combination of semisolid metal powder processing and powder metallurgy is used to process and manufacture Al7075-Al2O3 composites with a high reinforcement fraction of > 40 vol.%. The effects of processing parameters on the microstructures and mechanical properties of the composite material are discussed in detail. The loading limits of the high volume Al2O3 reinforcement in Al7075 composites are identified and linked to the processing parameters. A methodology is introduced to estimate the consolidation temperature of Al7075 alloy using compaction testing. Al2O3 particles (the average particle size of 120 µm) were mechanically milled with Al7075 powder (the average particle size of 20 µm) for 10 min and 5 h using a high-energy planetary ball mill. The mixture was then compacted in the semisolid state at 615 °C under the compaction pressures of 50 MPa and 100 MPa. By increasing the milling time from 10 min to 5 h, the deformation of aluminum powders and the fracture of Al2O3 reinforcement particles occur, restricting the loading limit of reinforcement. The milling time also shows a dominant effect on the powder morphology, microstructure, and mechanical properties of Al7075-Al2O3 composites. Increasing compaction pressure from 50 to 100 MPa significantly improved the compressive strength of the composite from 218 to 652 MPa. Al7075-Al2O3 composite with 40 vol.% of reinforcing phase exhibits the highest hardness of 198.2 HV and 96.9% relative density when it is milled for 5 h and compacted at 100 MPa. However, this composite shows the highest strength of 652 MPa when it is milled for 10 min. By increasing the reinforcing phase to 50 vol.% and 60 vol.%, the hardness, density, and compressive strength of composites decreased. The composites with 60 vol.% of reinforcing phase appeared overloaded. Results show that semisolid metal powder processing has huge potential for the fabrication of high loading Al2O3 in Al7075 matrix with near theoretical density.

Development and tribological investigation of B4C reinforced AA5082 Aluminum alloy cast composites for automotive applications

“…This raised the requisite of ceramic and composites to produce various components, especially in the sectors of aerospace, defense and automobile. In the past few decades, Aluminum matrix composites have come up as one of the most reliable and explored materials due to their top-notch properties thermal conductivity, good corrosive resistance, and density [1][2][3][4][5][6]. Though, the wear-resistant property of the aluminum composites is susceptible [7].…”

Influence of aging process and reinforcement ratio on physical and mechanical properties of carbonized aramid reinforced Al7075 materials

“…2 Al7075, which is an aluminum alloy, is one of the important materials used in the aircraft and automotive industries due to its well-designed production methods, which have the unique capacity to give the desired properties in the design of machine elements. 3,4 Production methods utilized for the improvement of aluminum metal matrix composites (AMMC) with the contributions of various researchers; mixing casting, 5 powder metallurgy, 6 spray atomization and co-deposition, plasma spraying and compression casting. 7 Abou El-khair 8 and Tian et al 9 stated that the squeeze casting method provides advantages such as high density, low porosity, good microstructure, coaxial structure, and enhanced mechanical properties 1 compared to traditional casting techniques.…”

The Effect of Powder Temperature on Semi-Solid Powder Rolling AA2024 Based on Experiments and Numerical Simulation

“…Semi-solid powder forming (SSPF), with advantages of fine grains, net shaping, a simple process and so on [1][2][3][4], has been widely used to prepare excellent composites by many researchers in recent years [5][6][7][8]. Semi-solid powder rolling (SSPR) is a kind of SSPF [9][10][11], which is mainly used to produce alloy or composite strips with high performances in the automotive, aerospace, shipbuilding industries and so on [12][13][14].…”