Microstructure and pitting corrosion of 13CrNiMo weld metals

Bilmes, Pablo David; Llorente, C.; Huamán, L. Saire; Gassa, Liliana Mabel; Gervasi, C.A.

doi:10.1016/j.corsci.2005.10.009

Cited by 73 publications

(37 citation statements)

References 13 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…The retained austenite can have beneficial effects on the corrosion resistance, because it favors chromium and molybdenum carbonitrides dissolution, increasing the content of these elements in the matrix. According to Bilmes et al 21 the pitting corrosion mechanism can also be associated with crack propagation, in which cracks propagate from the martensite phase to the austenite phase, ductile and stable, making them difficult to spread. Thus, the higher austenite volume fraction in tempered conditions, the lower pitting susceptibility 5,22 .…”

Section: Resultsmentioning

confidence: 99%

Tempering Temperature Influence on 13Cr4Ni0.02C Steel Corrosion Resistance

et al. 2017

View full text Add to dashboard Cite

The thermal treatments employed in alloys are essential to obtaining desired microstructures and corrosion resistance properties. In this paper the low carbon martensitic steel 13Cr4Ni0.2C with different tempering temperatures was studied using potentiodynamic polarization technique in synthetic marine environment, in order to evaluate the effect of the tempering temperature on the steel corrosion resistance in an environment that simulates the conditions of use in oil and gas production. Microscopy results showed differences in the microstructure of tempered steel at low (620°C) and high (770°C) temperatures, indicating the appearance and extending of martensite laths with increasing temperature. Polarization tests showed that tempering temperature located between 620°C and 710°C indicated passive film formation and tempering temperatures of around 620 °C showed better resistance values to pitting corrosion.

show abstract

Section: Resultsmentioning

confidence: 99%

Tempering Temperature Influence on 13Cr4Ni0.02C Steel Corrosion Resistance

et al. 2017

View full text Add to dashboard Cite

show abstract

“…부식으로 인한 경제적 손실과 안전재해 사고를 유발 할 수 있 으므로 강의 용접부식에 대한 연구 결과 (Bilmes et al, 2006;Jeon, 1985;Jones, 1998;Lee et al, 2003;Moon et al, 2003;Raja et al, 1998;Tsay et al, 1997) (4) 표면의 조직이 미세할수록 내식성은 양호한 경향을 나타내었다.…”

Section: 또한 이들 강구조물이 가혹한 부식 환경하에 있을 때 용접부위가unclassified

Electrochemical Evaluation of Corrosion Property of Welded Zone of Seawater Pipe by DC Shielded Metal Arc Welding with Types of Electrodes

Lee¹,

Lee²,

Won³

et al. 2013

Journal of Ocean Engineering and Technology

View full text Add to dashboard Cite

ABSTRACT:The seawater pipes in the engine rooms of ships are surrounded by severely corrosive environments caused by fast flowing seawater containing chloride ions, high conductivity, etc. Therefore, it has been reported that seawater leakage often occurs at a seawater pipe because of local corrosion. In addition, the leakage area is usually welded using shielded metal arc welding with various electrodes. In this study, when seawater pipes were welded with four types of electrodes (E4311, E4301, E4313, and E4316)

show abstract

“…Esse efeito produz um aumento da tenacidade desses aços (Toussaint & Dufrane, 2002). O efeito dessa austenita, na resistência à corrosão, é polêmico e, ainda, não foi esclarecido (Kimura et al, 2001;Bilmes et al, 2006 A diminuição da resistência à corrosão, após o tratamento térmico de revenido, é atribuída à precipitação de carbonetos ricos em cromo nos contornos de grão e entre as ripas de martensita. A formação desses carbonetos provoca o empobrecimento de cromo na matriz adjacente (Truman, 1976).…”

Section: Discussõesunclassified

Efeito do revenido na resistência à corrosão dos aços inoxidáveis supermartensíticos

Camillo

Rovere

Aquino

et al. 2010

Rem: Rev. Esc. Minas

View full text Add to dashboard Cite

ResumoOs aços inoxidáveis supermartensíticos são utilizados nas indústrias de petróleo e gás, pois aliam boas propriedades mecânicas, soldabilidade e excelente resistência à corrosão. Eles são endurecidos pelo tratamento térmico de têmpera e, para otimizar suas propriedades mecânicas, são submetidos ao revenimento. Durante o revenimento, ocorre precipitação de fases, que, dependendo dos parâmetros temperatura e tempo, induz alterações indesejadas nas propriedades desses aços. Nesse trabalho, o objetivo foi estudar a microestrutura e a resistência à corrosão de um aço inoxidável supermartensítico em diferentes condições de revenido (550°C, 600°C e 650°C). Observou-se, na microestrutura da amostra revenida a 650°C, a formação de austenita e precipitados de cromo do tipo Cr 3 C 2 e Cr 7 C 3 . As curvas de polarização indicaram que o tratamento térmico infl uencia o comportamento anódico, modifi cando a região passiva e as características do fi lme passivo. O revenido altera a resistência à corrosão, com o grau de sensitização diminuindo com o aumento de temperatura de 550°C para 650°C, devido à recuperação das zonas empobrecidas de cromo. Palavras

show abstract

Microstructure and pitting corrosion of 13CrNiMo weld metals

Cited by 73 publications

References 13 publications

Tempering Temperature Influence on 13Cr4Ni0.02C Steel Corrosion Resistance

Tempering Temperature Influence on 13Cr4Ni0.02C Steel Corrosion Resistance

Electrochemical Evaluation of Corrosion Property of Welded Zone of Seawater Pipe by DC Shielded Metal Arc Welding with Types of Electrodes

Efeito do revenido na resistência à corrosão dos aços inoxidáveis supermartensíticos

Contact Info

Product

Resources

About