Microstructure of low-dose neutron-irradiated Si3N4 and SiAlON ceramics after thermal annealing

Nitride ceramics have been investigated for different applications in the nuclear industry, such as space nuclear power, fusion reactor diagnostics and plasma heating, inert matrix fuels, and accident tolerant fuels. Although thermal conductivity remains one of the most important properties to track following irradiation, traditional techniques such as laser flash and xenon flash are limited to bulk sample characterization, which requires lengthy and cost-consuming neutron irradiation. This work used spatial domain thermoreflectance (SDTR) for the micrometer-scale measurement of thermal conductivity in 15 MeV Ni ion-irradiated silicon nitride and zirconium nitride from 1 to 50 dpa and 300 to 700 °C. The SDTR-measured unirradiated thermal conductivity was found to be consistent with the published data on bulk samples. Electrically conductive ZrN exhibits modest reduction after irradiation which is minimal at the highest irradiation temperatures. In electrically insulating Si3N4, the reduction is more significant and unlike ZrN, the reduction remains significant even at a higher irradiation temperature. The thermal resistance evolution following irradiation was compared with lattice swelling, which was determined using grazing incidence x-ray diffraction, and radiation-induced defects were observed using transmission electron microscopy. A saturation value was observed between 15 and 50 dpa for thermal conductivity degradation in both nitride ceramics and a direct correlation with high-temperature defect recombination was observed, as well as the potential presence of additional carrier scattering mechanisms.

show abstract

scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.

Contact Info

customersupport@researchsolutions.com

10624 S. Eastern Ave., Ste. A-614

Henderson, NV 89052, USA

This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.

Blog Terms and Conditions API Terms Privacy Policy Contact Cookie Preferences Do Not Sell or Share My Personal Information

Made with 💙 for researchers

Part of the Research Solutions Family.

Microstructure of low-dose neutron-irradiated Si3N4 and SiAlON ceramics after thermal annealing

Cited by 3 publications

References 17 publications

Effect of ion treatment on the structure and properties of ceramic materials (review)

Effect of ion treatment on the structure and properties of ceramic materials (review)

Properties and microstructure evolution of silicon nitride and zirconium nitride following Ni ion irradiation

Thermal conductivity evaluation of ion irradiated Si3N4 and ZrN ceramics using spatial domain thermoreflectance

Contact Info

Product

Resources

About