Minimising Defect Formation in Sand Casting of Sheet Lead: A DoE Approach

Abstract

Sand casting of lead sheet is a traditional manufacturing process used up to the present due to the special features of sand cast sheet such as their attractive sheen. Similarly to any casting process, sand casting of lead sheet suffers from the presence of surface defects. In this study, a surface defect type, hereby referred to as ‘grooves’, has been investigated. The focus has been laid on the identification of the main factors affecting defect formation in this process. Based on a set of screening experiments performed using Scanning Electron Microscopy (SEM) as well as the existing literature, a number of factors affecting the formation of such defects was identified and their corresponding significance was estimated using the Analysis of Variance (ANOVA) technique. The obtained results suggest that the most significant factor affecting defect formation in sand casting of lead sheet is the composition of the moulding mixture. Defect formation was also proven to be dependent on the sand grain fineness, the quality of the melt and some of the interactions between the aforementioned process parameters. Finally, an optimal set of process parameters leading to the minimisation of surface defects was identified.

Point Cloud Based Model-free Path Planning Method for grinding Large Complex Forging Parts

“…Large complex forgings play a vital role as major load-bearing components in industries such as energy, ships, transportation, and more [1]. After the forging process, various random defects of different sizes, such as parting lines, flashes, oxide skins, and local deformations, remain and need to be addressed through grinding as an essential post-processing procedure for large forgings [2].…”

Minimizing the Casting Defects in High Pressure Die Casting Using Taguchi Analysis

“…Similarly, Hassasi et al [36] and Souissi et al [37] investigated the effects of squeeze casting process parameters on the microstructure and mechanical properties of Aluminum alloy using a DOE approach based on the Taguchi method. Prabhakar et al [38] used DOE, i.e., ANOVA, to identify the most significant process parameters during the formation of grooves manufactured by the sand casting process. An optimal set of parameters was proposed to minimize defects in the final product.…”