Multifunctional Anionic Zn(II)-MOF for Selective CO₂ Adsorption, Cationic Dye Removal, and Luminescence-Based pH Sensing

Abstract

An anionic 2-fold interpenetrated 3D framework, {(pbisoixH2)2[Zn2(μ4-TDBAT)2]·S} n (ESOGU-2), referred Eskisehir Osmangazi University (TDBAT: 5,5′-((thiophene-2,5-dicarbonyl)­bis­(azanediyl))­diisophthalate, pbisoixH2: protonated 1,4-bis­(2-isopropylimidazol-1ylmethyl)­benzene) was prepared and characterized by diverse techniques. X-ray result demonstrated that the anionic framework was formed by Zn­(II) ions and TDBAT4– and its charge balance was kept by protonated pbisoixH2. Due to the porous structure of ESOGU-2 and stability in water with different pH ranges, CO2 and dye adsorption studies were performed. The results displayed that ESOGU-2 possessed a high Brunauer–Emmett–Teller (BET) surface area (1112.77 m2 g–1) despite the interpenetration and a selective CO2 (19.02%) adsorption over N2 (0.342%) at 100 kPa and 273 K due to dipole–quadrupole interactions. Furthermore, ESOGU-2 removed the cationic methyl violet dye from an aqueous solution, while anionic methyl orange was not adsorbed by ESOGU-2 due to its anionic framework. In addition, ESOGU-2 displayed turn-on and turn-off luminescence behaviors depending on the amount of H+ and OH– ions in the aqueous solution. ESOGU-2 showed high emission intensity in the pH range of 2.5–4.75 but displayed weak emission after pH = 6.

Two-Dimensional Cu-Based MOF for Selective Staining of the Cellular Nucleus through Fluorescence Imaging and Selective Sorption of Dye Molecules in Aqueous Medium

“…Upon excitation at 370 nm, compound 1 exhibits a broad peak centered at 525 nm. The observed emission comes out due to the intraligand transitions (π* → π and π* → n ) of the bonded organic ligands with the metal center. − The excitation spectra of the aqueous dispersion of compound 1 and pamoate ligand were recorded using an emission wavelength value of 525 nm (see Figure S9 in the SI).…”